. 2014 Jun 18;70(Pt 7):i41. doi: 10.1107/S1600536814013658
K1—O1i 2.956 (16) Zr1—O1xiii 2.070 (14)
K1—O2ii 3.165 (14) Zr1—O2xiv 2.098 (14)
K1—O4ii 3.325 (14) Zr2—O4 2.036 (12)
K1—O1iii 2.956 (16) Zr2—O3i 2.041 (16)
K1—O2iv 3.165 (14) Zr2—O4xi 2.036 (12)
K1—O4iv 3.325 (14) Zr2—O3iii 2.041 (16)
K1—O1v 2.956 (16) Zr2—O4xiii 2.036 (12)
K1—O2vi 3.165 (14) Zr2—O3v 2.041 (16)
K1—O4vi 3.325 (14) Ni1—O2xii 2.098 (14)
K2—O3ii 2.973 (15) Ni1—O1xiii 2.070 (14)
K2—O2vii 3.026 (16) Ni1—O2xiv 2.098 (14)
K2—O4ii 3.127 (15) Ni1—O1xi 2.070 (14)
K2—O4vii 3.332 (15) Ni1—O1 2.070 (14)
K2—O3iv 2.973 (15) Ni1—O2x 2.098 (14)
K2—O2viii 3.026 (16) Ni2—O4 2.036 (12)
K2—O4iv 3.127 (15) Ni2—O3v 2.041 (16)
K2—O4viii 3.332 (15) Ni2—O3i 2.041 (16)
K2—O3vi 2.973 (15) Ni2—O4xi 2.036 (12)
K2—O2ix 3.026 (16) Ni2—O3iii 2.041 (16)
K2—O4vi 3.127 (15) Ni2—O4xiii 2.036 (12)
K2—O4ix 3.332 (15) P1—O3 1.530 (18)
Zr1—O1 2.070 (14) P1—O4 1.523 (13)
Zr1—O2x 2.098 (14) P1—O2 1.515 (15)
Zr1—O1xi 2.070 (14) P1—O1 1.493 (16)
Zr1—O2xii 2.098 (14)
O1—Zr1—O2x 93.2 (5) O1—Ni1—O2x 93.2 (5)
O1—Zr1—O1xi 90.6 (6) O1—Ni1—O1xi 90.6 (6)
O1—Zr1—O2xii 175.9 (5) O1—Ni1—O2xii 175.9 (5)
O1—Zr1—O1xiii 90.6 (6) O1—Ni1—O1xiii 90.6 (6)
O1—Zr1—O2xiv 87.7 (6) O1—Ni1—O2xiv 87.7 (6)
O1xi—Zr1—O2x 87.7 (6) O1xi—Ni1—O2x 87.7 (6)
O2x—Zr1—O2xii 88.6 (5) O2x—Ni1—O2xii 88.6 (5)
O1xiii—Zr1—O2x 175.9 (5) O1xiii—Ni1—O2x 175.9 (5)
O2x—Zr1—O2xiv 88.6 (5) O2x—Ni1—O2xiv 88.6 (5)
O1xi—Zr1—O2xii 93.2 (5) O4xi—Ni2—O4xiii 87.5 (5)
O1xi—Zr1—O1xiii 90.6 (6) O3v—Ni2—O4xi 170.8 (5)
O1xi—Zr1—O2xiv 175.9 (5) O3iii—Ni2—O4xiii 84.5 (5)
O1xiii—Zr1—O2xii 87.7 (6) O3iii—Ni2—O3v 92.1 (5)
O2xii—Zr1—O2xiv 88.6 (5) O3v—Ni2—O4xiii 96.5 (5)
O1xiii—Zr1—O2xiv 93.2 (5) O3i—Ni2—O3iii 92.1 (5)
O3i—Zr2—O4 96.5 (5) O3i—Ni2—O4 96.5 (5)
O4—Zr2—O4xi 87.5 (5) O4—Ni2—O4xi 87.5 (5)
O3iii—Zr2—O4 170.8 (5) O3iii—Ni2—O4 170.8 (5)
O4—Zr2—O4xiii 87.5 (5) O4—Ni2—O4xiii 87.5 (5)
O3v—Zr2—O4 84.5 (5) O3v—Ni2—O4 84.5 (5)
O3i—Zr2—O4xi 84.5 (5) O3i—Ni2—O4xi 84.5 (5)
O3i—Zr2—O3iii 92.1 (5) O3iii—Ni2—O4xi 96.5 (5)
O3i—Zr2—O4xiii 170.8 (5) O3i—Ni2—O4xiii 170.8 (5)
O3i—Zr2—O3v 92.1 (5) O3i—Ni2—O3v 92.1 (5)
O3iii—Zr2—O4xi 96.5 (5) O3—P1—O4 109.5 (8)
O4xi—Zr2—O4xiii 87.5 (5) O1—P1—O2 108.1 (9)
O3v—Zr2—O4xi 170.8 (5) O1—P1—O3 110.1 (9)
O3iii—Zr2—O4xiii 84.5 (5) O1—P1—O4 109.9 (9)
O3iii—Zr2—O3v 92.1 (5) O2—P1—O3 109.7 (8)
O3v—Zr2—O4xiii 96.5 (5) O2—P1—O4 109.5 (9)
O1xi—Ni1—O2xii 93.2 (5) Zr1—O1—P1 135.2 (10)
O1xi—Ni1—O1xiii 90.6 (6) Ni1—O1—P1 135.2 (10)
O1xi—Ni1—O2xiv 175.9 (5) Zr1xv—O2—P1 168.8 (10)
O1xiii—Ni1—O2xii 87.7 (6) Zr2xvi—O3—P1 153.7 (9)
O2xii—Ni1—O2xiv 88.6 (5) Zr2—O4—P1 156.8 (9)
O1xiii—Ni1—O2xiv 93.2 (5) Ni2—O4—P1 156.8 (9)