Figure 1.

Figure 1

Mechanical characterization of photoPDMS. (a&b) Strain-stress curves generated from tensile testing of 1:10 (a) and 1:30 (b) photoPDMS prepared after different UV light exposure time, as indicated. 1:10 and 1:30 photoPDMS was baked at 110°C for 40 hr and 20 min, respectively. Slopes of linear fittings of the strain-stress raw data were quantified as the bulk Young’s Modulus E of photoPDMS. (c&d) Young’s Modulus E of 1:10 (c) and 1:30 (d) photoPDMS as a function of UV light exposure time. 1:10 and 1:30 photoPDMS was baked at 110°C for 40 hr and 20 min, respectively.