Table 1.
HAP/Lig, wt % Lig | Thermal Treatment | Ca | P | C | Ca/P |
---|---|---|---|---|---|
HAP | non-sintered | 19.4 | 11.3 | 7.2 | 1.72 |
sintered | 16.5 | 5.5 | 21.7 | 3.00 | |
0.5 | non-sintered | 19.1 | 11.3 | 8.2 | 1.69 |
sintered | 18.4 | 7.9 | 15.9 | 2.33 | |
1 | non-sintered | 19.3 | 10.8 | 10.5 | 1.79 |
sintered | 18.7 | 8.9 | 11.3 | 2.10 | |
3 | non-sintered | 18.4 | 12.0 | 11.7 | 1.53 |
sintered | 18.8 | 10.8 | 12.9 | 1.74 | |
10 | non-sintered | 15,8 | 10,3 | 21,3 | 1.53 |
sintered | 17,1 | 9,6 | 18,9 | 1.78 |