. 2014 Sep 3;6(18):16283–16288. doi: 10.1021/am504486r

Figure 2.

Figure 2

(Solid line) Experimental 1D synchrotron SAXS profile of shear-oriented PS–PLA monolith at 25 °C and (dashed line) simulated form factor scattering curve generated for cylinders with a 11.8 nm radius (value extracted from the experimental SAXS profile). The black triangles indicate the expected reflections for a cylindrical morphology (√1; √3; √4; √7; √9). Corresponding TEM images of the material obtained (left) perpendicularly and (right) parallel to the shear direction (The PS matrix was stained by RuO4 vapors).