. 2015 Jan 12;16(1):1590–1612. doi: 10.3390/ijms16011590

Table 1.

Texture parameters of the precursors, carbon C800 and TiO₂/C materials prepared in a 1:1 Manihot: TiO₂ ratio by variant (a) as depicted in Figure 1, and the corresponding isotherms are shown in Figure 2.

Material		Specific Surface (m²·g⁻¹)			V_μ, cm³·g⁻¹	V_tot, cm³·g⁻¹	Average Pore Diameter, nm
Material		BET	S₀^t (%)	S_e^t	V_μ, cm³·g⁻¹	V_tot, cm³·g⁻¹	Average Pore Diameter, nm
Precursors	TiO₂	58	-	-	-	0.678	-
Precursors	raw Manihot	72 ^a	-	-	-	-	-
Carbon	C800	449	318 (71)	130	0.160	0.263	2.6
TiO₂/C	MT	226	100 (44)	126	0.051	0.712	6.9
	MT-W	493	245 (50)	248	0.125	0.611	5.4
	MT-G	87	24 (28)	63	0.013	0.353	17.6

^a measured by the adsorption of methylene blue from solution.