Table 2.

The parameters of the conduction process in SPS LLT garnet nanoceramics

T (K)	σ dc (S/cm)	ω H (Hz)	n	n c (cm −3 )	μ (cm 2  V −1  s −1 )	D (cm 2  s −1 )
SPS-850
230	1.15 × 10−10	4.87 × 102	0.60	6.08 × 1020	1.18 × 10−12	2.34 × 10−14
240	4.16 × 10−10	1.68 × 103	0.60	6.62 × 1020	3.92 × 10−12	8.11 × 10−14
250	1.45 × 10−9	5.21 × 103	0.60	7.78 × 1020	1.16 × 10−11	2.51 × 10−13
260	5.32 × 10−9	1.93 × 104	0.61	7.99 × 1020	4.16 × 10−11	9.31 × 10−13
270	1.75 × 10−8	6.10 × 104	0.62	8.65 × 1020	1.26 × 10−10	2.94 × 10−12
SPS-875
220	1.47 × 10−10	5.90 × 102	0.61	6.13 × 1020	1.50 × 10−12	2.84 × 10−14
230	5.37 × 10−10	2.12 × 103	0.61	6.50 × 1020	5.16 × 10−12	1.02 × 10−13
240	1.83 × 10−9	6.48 × 103	0.61	7.56 × 1020	1.51 × 10−11	3.12 × 10−13
250	6.44 × 10−9	2.32 × 104	0.62	7.74 × 1020	5.19 × 10−11	1.12 × 10−12
260	2.18 × 10−8	7.33 × 104	0.62	8.64 × 1020	1.57 × 10−10	3.53 × 10−12
SPS-900
240	1.28 × 10−10	4.88 × 102	0.60	7.02 × 1020	1.14 × 10−12	2.35 × 10−14
250	4.63 × 10−10	1.83 × 103	0.62	7.07 × 1020	4.09 × 10−12	8.80 × 10−14
260	1.69 × 10−9	6.36 × 103	0.64	7.71 × 1020	1.37 × 10−11	3.06 × 10−13
270	5.97 × 10−9	2.30 × 104	0.66	7.81 × 1020	4.77 × 10−11	1.11 × 10−12
280	1.85 × 10−8	6.83 × 104	0.64	8.45 × 1020	1.37 × 10−10	3.30 × 10−12

The values of the dc conductivity σ _dc, the hopping frequency ω _H, the exponent n, the concentration of mobile Li ions n _c, the mobility μ, and the diffusion coefficient D are summarized for the SPS LLT garnet nanoceramics at different temperatures.