Table 2.
SF:P(LLA_CA) (8% w/v) | Nanofiber diameter (nm) | Specimen thickness (μm) | Contact angle at 20 seconds (degrees) | Tensile strength (MPa) |
---|---|---|---|---|
100:0 | 147±24 | 30±9.53 | 38.36±0.41 | 1.90±0.75 |
75:25 | 226±31 | 56±5.12 | 49.03±0.67 | 2.39±0.22 |
50:50 | 255±37 | 62.5±7.93 | 62.93±0.50 | 5.29±0.66 |
25:75 | 226±24 | 56±4.20 | 71.58±0.15 | 9.39±0.69 |
0:100 | 542±107 | 128±6.65 | 125.78±0.02 | 7.47±0.38 |
Note: Data are shown as the mean ± standard deviation, unless otherwise specified.
Abbreviations: SF, silk fibroin; P(LLA-CL), poly(l-lactic acid-co-ε-caprolactone).