Table 1.

Summary of experimental data

	Sample No.	L (mm)	A (mm2)	T (°C)	έ × 104 (s−1)	Δε × 103	E (MPa)	R 2	Failure stress (MPa)
PEG400	1	35.00	8.84	−149.3	0.73	0.07	2279	0.999	6.99
	2	31.66	7.54	−145.0	0.80	3.60	2475	0.999	11.21
	3	26.48	8.04	−139.8	0.96	1.91	2006	0.999	9.67
	4	26.00	7.04	−143.0	0.98	2.34	2479	1.000	12.58
	5	30.42	8.84	−139.8	0.84	2.41	2001	0.999	12.44
	6	23.26	8.27	−143.9	1.09	6.21	2426	0.999	15.91
Average	28.80	8.10	−143.46	0.90	2.07	2248 ± 224 a	0.999	10.58 ± 3.01 a
7.05 M DMSO	1	28.00	9.40	−150.0	0.91	6.35	922	0.999	7.38
	2	25.70	10.33	−147.5	0.99	5.58	950	0.999	9.80
	3	31.34	10.72	−153.9	0.81	6.88	1011	0.999	12.22
	4	25.93	8.98	−142.9	0.98	10.30	1495	1.000	15.68
	5	31.21	6.78	−167.7	0.81	1.83	2955	0.999	14.81
	6	21.68	9.44	−146.2	1.17	7.88	1839	0.999	13.89
	7	30.48	11.30	−148.6	0.83	4.99	2240	0.999	N/A
	8	24.67	7.26	−163.1	1.03	4.61	2700	0.999	18.01
	9	22.71	12.50	−138.2	1.12	8.15	1631	0.999	12.44
Average	28.44	9.24	−152.39	0.90	6.19	2143 ± 754 a	0.999	11.98 ± 3.36 a
1,3-CHD	1	27.39	10.49	−151.0	0.93	2.32	1480	1.000	9.59
	2	22.46	8.03	−142.8	1.11	7.03	2080	0.999	17.96
	3	24.48	8.11	−150.0	1.04	2.69	2310	1.000	10.07
	4	27.19	8.31	−144.3	0.93	3.06	1777	0.999	6.65
	5	25.63	8.66	−145.5	0.99	2.46	2448	0.999	15.92
Average	25.43	8.72	−146.7	1.00	3.51	2019 ± 394 a	0.999	12.04 ± 4.72 a
2,3BD	1	21.31	7.21	−148.3	1.19	2.14	2940	0.999	12.83
	2	28.31	10.71	−143.3	0.90	1.77	2868	0.999	10.05
	3	29.07	8.80	−146.0	0.87	1.66	3012	1.000	19.72
	4	22.68	6.93	−153.0	1.12	3.95	2811	0.999	18.68
	5	19.35	8.15	−144.2	1.31	5.10	2062	0.999	15.64
	6	24.24	9.79	−147.0	1.04	5.27	1688	0.999	14.65
	7	24.26	8.67	−141.0	1.05	5.22	2298	0.999	19.32
	8	19.07	8.62	−151.7	1.33	1.92	1675	0.999	12.19
	9	24.01	8.52	−149.8	1.06	7.38	2416	0.999	16.46
Average	23.59	8.60	−147.14	1.10	3.82	2419 ± 525 a	0.999	15.50 ± 3.39 a
Frozen	1	23.29	9.79	−146.1	1.09	4.84	1226	0.996	5.25

^aStandard deviation