Skip to main content
. Author manuscript; available in PMC: 2015 Sep 25.
Published in final edited form as: J Mater Chem B. 2015 Feb 18;3(14):2858–2866. doi: 10.1039/C4TB01880J

Fig. 2.

Fig. 2

(a) TEM images of P(BCe) NPs prepared from the photo polymerization of spherical assemblies at −10°C, these assemblies were formed by using (a) 40.0 mM of BM and CM. (b) Typical SEM of a P(BCe) NP and EDX elemental mapping (C, B and N) of the nanoparticle. (C) TEM image of P(BCe-MAPEG) NPs prepared by using BCe assemblies that were obatined from (d) 40.0 mM of BM and CM. (d) Typical SEM of a P(BCe-MAPEG) N and EDX elemental mapping (C, B and N) of the nanoparticle. (e) Diameter evolution of P(BCe) NPs in water solution at neutral pH under thermal cycling. (f) Diameter evolution of P(BCe) NPs in acidic water solution or in the presence of D-glucose with pH=5.5.