. 2015 Sep 29;10:375. doi: 10.1186/s11671-015-1062-5

Polarization Properties in Apertureless-Type Scanning Near-Field Optical Microscopy

Takayuki Ishibashi 1,, Yongfu Cai 1
PMCID: PMC4586183  PMID: 26415540

Abstract

Polarization properties of apertureless-type scanning near-field optical microscopy (a-SNOM) were measured experimentally and were also analyzed using a finite-difference time-domain (FDTD) simulation. Our study reveals that the polarization properties in the a-SNOM are maintained and the a-SNOM works as a wave plate expressed by a Jones matrix. The measured signals obtained by the lock-in detection technique could be decomposed into signals scattered from near-field region and background signals reflected by tip and sample. Polarization images measured by a-SNOM with an angle resolution of 1° are shown. FDTD analysis also reveals the polarization properties of light in the area between a tip and a sample are p-polarization in most of cases.

Keywords: a-SNOM, Polarization property, FDTD, Jones matrix

Background

Recently, nano-optics are attracting great attentions not only for measuring physical properties such as optical responses [1, 2], Raman scattering [3], and magnetic properties but also for reactions of molecules and/or controlling of spins. In those cases, polarization states in nano-optics are very important, because those phenomena are dependent on the polarization of light. For example, spin manipulation with light is attracting attentions because light may have abilities of controlling the direction of magnetization in a time scale of several tenth nanoseconds. Stanciu et al. reported that magnetization direction of GdFeCo is optically switched by a 40 fs circularly polarized light (CPL) pulse [4]. Satoh et al. demonstrated the spin-wave emission and the directional control of propagation using the CPL or linearly polarized light (LPL) [5]. These new phenomena may lead to controlling single spin with light. On the other hand, CPL has been also used to measure circular dichroism (CD) due to the geometric and electromagnetic chiral properties of single molecule [6], biomolecules [7], and singe-wall carbon nanotube [8]. In those cases, obviously, each single molecule can be selectively investigated if nano-sized CPL is available.

For high resolved polarization imaging with a spatial resolution of ~10 nm, scanning near-field optical microscopies (SNOM) have been developed in the 1990s [912]. Aperture-type SNOMs using optical probe having an aperture on top of tapered optical fiber with metal were extensively studied, because it was considered that polarization properties were maintained and background signal was relatively small. Magneto-optical (MO) measurements that measure optical responses of magnetic materials for circular polarization are one of the most important purpose at that time [1122], because size of magnetic recording marks had became smaller than the wavelength of the visible light. Several groups use aperture-type optical fiber probes collecting the evanescent wave, which is referred to as a transmission-mode MO-SNOM. However, there are disadvantages. When the evanescent wave propagates through the optical probes, the light intensity decreases extremely, the polarization of the wave is deteriorated, and the spatial resolution of the imaging was limited to the size of the aperture, which is typically larger than 50 nm. In addition, it was difficult to measure opaque materials in reflection-mode, because the thickness of metallic coating contributes to enlargement of probe end.

Another type of SNOM, apertureless-type SNOM (a-SNOM), has also been developed, in which cantilever tips for atomic force microscopy were used instead of the optical fibers probe with an aperture. In a-SNOM, the scattered light generated at the area where evanescent waves are formed between the tip’s extremity and the sample’s surface. Considering the principle of a-SNOM, we can expect higher spatial resolution depending on the radius of tips, which is smaller than 10 nm in the commercially available tip, with higher intensity and good polarization properties. In addition, it is considered that a-SNOM is suitable for measurements of opaque materials, since there is no obstacle around the extremity of tips. One of the most successful applications of a-SNOM is tip-enhance Raman scattering spectroscopy [2327]. On the other hand, polarization property of a-SNOM has not been sufficiently understood yet. In this paper, we report the polarization properties of a-SNOM, including experimental and simulation results.

Methods

a-SNOM setup

The a-SNOM setup is illustrated in Fig. 1. We used a commercial scanning probe microscopy (SPM) from Seiko Instrument Inc., model SPI3800N probe station and SPA300 unit, as a base instrument, and during the experiment process, we selected the dynamic force mode (DFM). The tip is SI-DF3P2 SII NanoTechnology Inc., made of silicon having an extremity’s radius of 7 nm and a resonant frequency Ω of 77 kHz. A laser beam (TC20-4030-4.5/15, NEOARK) with a wavelength of 408 nm propagates through a half-wave plate and a polarizer to ensuring a certain polarization direction, i.e., either s- or p-polarization direction, later is passing to a prism-type beam splitter and is finally focused at the tip apex by a plate-type lens. An angle between a sample surface and the incident beam is 45°. A scattered beam from the tip and the sample’s surface is collected by the same lens, reflected by the beam splitter, and is passing through an imaging lens. Signals were detected using a lock-in detection technique and demodulated at frequencies Ω or 2Ω.

Fig. 1.

Fig. 1

A schematic of a-SNOM developed in our study [28]

FDTD simulation

The finite-difference time-domain (FDTD) method is a straightforward calculation of Maxwell’s equations in both time and space. In our simulation, we used a commercial soft, FullWAVE (RSoft Design Group, Inc.). Figure 2 shows a schematic drawing of a simulation model used in this study. A conical probe made of silicon (n = 5.476 + i0.310 at the wavelength of 408 nm) with an extremity’s radius of 7 nm and a solid angle of 15° was located above the Cr (n = 1.80 + i3.61 at the wavelength of 408 nm) film. A distance between the probe and the Cr was 10 nm. A pulse plane wave with a wavelength of 408 nm and a pulse width of 2.1 fs impinged on the tip and the sample with an incident angle of 45°. 3D monitors were located in front of light source to record the electric field of incident light and in the behind of light source to record the electric field of scattered light. The size of our model was 3 × 3 × 3 μm3, using 3 × 3 × 3 nm3 cell. The probe was set with normal to the Cr surface to study fundamental polarization properties of a-SNOM, although there was an inclination of approximately 10° in the actual experiment [2930].

Fig. 2.

Fig. 2

A model of a-SNOM used for our simulation [29]

Results and Discussion

We measured a chromium film deposited on a quartz substrate with a checker pattern with a thickness of 20 nm and a period of 2 × 2 μm2. Figure 3 shows a topographic image and two SNOM images of the chromium pattern measured with the s-polarized illumination [28]. Figure 3b, c was measured at demodulation frequencies of Ω and 2Ω, respectively. In those SNOM images, the checker pattern corresponding to the topography in Fig. 3a is clearly observed. We found that the intensity of area of chromium film (higher parts) is higher than that of quartz area (lower parts), and they showed opposite sign of phase ϕ for the chromium and the quartz. This result indicates that the signal depends on not only the reflectivity but also the phase. Therefore, we consider that the contrast obtained in those SNOM images is due to difference in the complex permittivity of the materials. In Fig. 3c, a dark area surrounding the chromium patterns is observed. We believe this is due to the edge darkening effect. Spatial resolution was determined to be 14 nm by measuring a cross section of SNOM images measured at 2Ω.

Fig. 3.

Fig. 3

a An AFM image and b, c SNOM images of Cr pattern on quartz substrate. b and c were measured with demodulation frequency of Ω and 2Ω, respectively [28]

To analyze polarization properties of the a-SNOM, we measured the intensity of SNOM signal with an analyzer. Figure 4 shows polar plots of the intensities measured at demodulation frequency of 2Ω with linearly polarized incident lights with azimuth angles of 0° to 90° plotted as a function of the analyzer angles. Red solid lines show ideal linearly polarizations of the azimuth angles of the incident lights. In Fig. 4a, j, corresponding to s- and p-polarizations, respectively, the polarizations of measured data coincide with those of the incident light, suggesting the polarization of light was maintained. However, polarization properties of SNOM signals showed different properties except for s- and p-polarizations, as shown in Fig. 4bi. For example, clover-shaped patterns were observed in some cases, Fig. 4d, e, g, and h, indicating that measured signals consisted of two or more components with different polarizations as described below.

Fig. 4.

Fig. 4

aj Polar plots for SNOM intensities measured with various angles of analyzer. Dots are measured data, and red solid lines show linearly polarization expressed by cos2 θ

Since the polarization seems to be maintained in the case of s- and p-polarization illuminations, we measured polarization SNOM images in order to confirm it. Figure 5 shows an AMF image and SNOM images of a Cr pattern on quart substrate measured with s-polarization illumination. Figure 5b was measured with the analyzer angles of 0°, 20°, and 40° as indicated on right side of the figure, where the angle was changed during the measurement. The intensity of the SNOM image was clearly decreased with the analyzer angle was increased, which corresponded to the result shown in Fig. 4a. Furthermore, we measured a SNOM image with the analyzer angles of 45°, 46°, and 47° as shown in Fig. 4c. As a result, the polarization images were successfully measured with the angle resolution better than 1°.

Fig. 5.

Fig. 5

a An AFM image and b, c SNOM images of a Cr pattern on quart substrate measured with various angles of the analyzer shown in the right side of the images

Although polarization images were successfully measured in Fig. 5, we have to mention that the measured signals consist of two or more polarized light. Figure 6 shows the intensity and the phase measured by the lock-in amplifier plotted as a function of the angle of the analyzer. The intensity changed with the angle of the analyzer and had peaks, corresponding to the clover-shaped pattern in Fig. 4. It is found that the phase suddenly changed and the angle difference was 180°, suggesting that there were at least two different signals involved. For example, considering SNOM signal has a maximum intensity when the tip approaches close to a sample surface in DFM mode, the other signal should have a maximum intensity when the tip separates from the sample surface. Therefore, we assume that measured signals consisted of two polarized lights, SNOM signal and background signal, described in an equation,

I=EN2cos2θ+ψN+βN+EB2cos2θ+ψB+βB 1

where E is strength of electric field, θ is the angle of the analyzer, ψ is the azimuth angle of the polarized light, β corresponds to ellipticity, and N and B denote SNOM signal from near-field region and background signal, respectively. In this analysis, we also assume the background signal was a light reflected by a tip made of Si and a sample made of Cr. As a consequence, we can obtain the parameter, ψB and βB, using optical constants of Si and Cr. Once the polarization of the background signal was obtained, we can determine the other parameters by fitting of measured data. An example of the fitting is shown in Fig. 7. The measured data shown in Fig. 7a can be decomposed into two polarized light, SNOM signal in blue and background signal in red, as shown in Fig. 7b. In all cases, SNOM signals were successfully deduced by the fitting procedure, and the results summarized in Fig. 8. show azimuth angles of SNOM signals measured for the azimuth angle of the incident light of 60° and demodulation frequencies Ω and 2Ω are plotted together with a result obtained by the FDTD simulation [30]. In the case of Ω, the azimuth angles of SNOM signals gradually increased with the angle of the azimuth of the incident light, which agreed with the result by FDTD. On the other hand, data for 2Ω agreed with FDTD for the angle below 50°, but it behaved differently for 60°–80°. We can not explain the reason of the difference, but it may be due to the shape of the apex of the tip, because the measurement at a demodulation frequency 2Ω has stronger distance dependence than that at Ω.

Fig. 6.

Fig. 6

Intensity and phase of SNOM signal measured with the lock-in amplifier

Fig. 7.

Fig. 7

a A polarplot of SNOM signal plotted as a function of angle of analyzer and b a result of decomposition

Fig. 8.

Fig. 8

Azimuth angles of SNOM signals deduced by the fitting plotted as a function of azimuth angles of the incident light, together with a result of FDTD simulation

The ratios of the SNOM signals to the background signals measured for the azimuth angles of the incident light of 60° were plotted as a function of the analyzer angles in Fig. 9a. It was found that there are peaks at 140° and 320°, which are quite different from the azimuth angles of the incident light of 60°. If this is true, SNOM could be measured with good S/N ratio at those peak positions. In order to prove the validity of our analysis, we measured SNOM images of the Cr pattern with various angles of analyzer, 0°, 50°, 130°, 140°, 150°, and 230° as shown in Fig. 9b. Clear SNOM image was obtained for 0° and 150°, which is close to the peak position in Fig. 9a. On the contrary, the SNOM images measured for 50° and 230°, close to the azimuth angle of the incident light, suffered from noise due to background signals. From these results, we can conclude that our analysis is valid.

Fig. 9.

Fig. 9

a Ratios of SNOM signals to background signals plotted as a function of the analyzer, and b SNOM images of a Cr pattern on quart substrate measured with various angles of analyzer indicated in (a), 0°, 50°, 130°, 140°, 150°, and 230°

From the FDTD simulation, we also found that the a-SNOM system can be described by Jones matrix as described [30],

T=3.95400exp0.710i 2

This result indicates that a-SNOM maintains the polarization of light and works as a wave plate. However, we found that the polarization state in the near-field region between the tip and the sample is only in p-polarization except for the case that both azimuth angle and ellipticity of the incident light is almost zero. Figure 10 shows strengths of electric filed components, Ex, Ey, and Ez, plotted as a function of the azimuth angles and the ellipticity of the incident light. In most of the cases, including the case of the circular polarization, strength of Ez was the largest, indicating that linear polarization is p-polarization. This result indicates the difficulty of measuring the optical responses due to circular polarization, such as CD and MO effect, by using a-SNOM, which is consistent with the theoretical prediction [31]. To overcome this problem, we need to consider another type of tip that can produce nano-sized circular polarized light [32].

Fig. 10.

Fig. 10

Electric filed components, E x, E y, and E z are plotted as a function of the azimuth angles and the ellipticity of the incident light

Conclusions

Polarization properties of apertureless-type scanning near-field optical microscope (a-SNOM) were studied. Polarization SNOM images were successfully measured with the spatial resolution of ~14 nm and the angle resolution better than 1°. We found that the polarization properties of optical signals could be decomposed into SNOM signal scattered from near-field region and background signal reflected by a tip and a sample. Signal to noise ratio was improved by choosing the angles of the incident light and the analyzer. We also found that a-SNOM worked as a wave plate described by Jones matrix and the polarization state of the electric field between a tip and a sample was p-polarization.

Acknowledgements

This research was supported by the National Institute of Information and Communications Technology (NICT) and KAKENHI, Grants-in-Aid for Scientific Research (B) (23310073).

Footnotes

Competing Interests

The authors declare that they have no competing interests.

Author’ Information

Department of Materials Science and Technology, Nagaoka University of Technology, 940–2188 Kamitomioka, Nagaoka, Niigta, Japan. Email: t_bashi@mst.nagaokaut.ac.jp. Web site: http://mst.nagaokaut.ac.jp/~t_bashi/ISHIBASHI_LAB/home.html

Authors’ Contributions

TI designed the a-SNOM measured all the samples in this articles. YC performed the FDTD simulation and data analysis. All the authors read and approved the final manuscript.

Contributor Information

Takayuki Ishibashi, Email: t_bashi@mst.nagaokaut.ac.jp.

Yongfu Cai, Email: yongfu_sai@mst.nagaokaut.ac.jp.

References

  • 1.Pan MY, Lin EH, Wang L, Wei PK. Spectral and mode properties of surface plasmon polariton waveguides studied by near-field excitation and leakage-mode radiation measurement. Nanoscale Res Lett. 2014;9:430. doi: 10.1186/1556-276X-9-430. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 2.Zhang P, Li S, Liu C, Wei X, Wu Z, Jiang Y, Chen Z. Near-infrared optical absorption enhanced in black silicon via Ag nanoparticle-induced localized surface plasmon. Nanoscale Res Lett. 2014;9:519. doi: 10.1186/1556-276X-9-519. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 3.Hayazawa N, Saito Y, Kawata S. Detection and characterization of longitudinal field for tip-enhanced Raman spectroscopy. Appl Phys Lett. 2004;85:6239–41. doi: 10.1063/1.1839646. [DOI] [Google Scholar]
  • 4.Stanciu CD, Hansteen F, Kimel AV, Kirilyuk A, Tsukamoto A, Itoh A, Rasing T. All-optical magnetic recording with circularly polarized light. Phys Rev Lett. 2007;99:047601. doi: 10.1103/PhysRevLett.99.047601. [DOI] [PubMed] [Google Scholar]
  • 5.Satoh T, Terui Y, Moriya R, Ivanov BA, Ando K, Saitoh E, Shimura T, Kuroda K. Directional control of spin-wave emission by spatially shaped light. Nat Photonics. 2012;6:662–6. doi: 10.1038/nphoton.2012.218. [DOI] [Google Scholar]
  • 6.Hassey R, Swain EJ, Hammer NI, Venkataraman D, Barnes MD. Probing the chiroptical response of a single molecule. Science. 2006;314:1437–9. doi: 10.1126/science.1134231. [DOI] [PubMed] [Google Scholar]
  • 7.Hendry E, Carpy T, Johnston J, Popland M, Mikhaylovskiy RV, Lapthorn AJ, Kelly SM, Barron LD, Gadegaard N, Kadodwala M. Ultrasensitive detection and characterization of biomolecules using superchiral fields. Nat Nanotechnol. 2010;5:783–7. doi: 10.1038/nnano.2010.209. [DOI] [PubMed] [Google Scholar]
  • 8.Peng X, Komatsu N, Bhattacharya S, Shimawaki T, Aonuma S, Kimura T, Osuka A. Optically active single-walled carbon nanotubes. Nat Nanotechnol. 2007;2:361–5. doi: 10.1038/nnano.2007.142. [DOI] [PubMed] [Google Scholar]
  • 9.Bezig E, Trautman JK, Harris TD, Weiner JS, Kostelak RL. Breaking the diffraction barrier: optical microscopy on a nanometric scale. Science. 1991;251:1468–70. doi: 10.1126/science.251.5000.1468. [DOI] [PubMed] [Google Scholar]
  • 10.Bezig E, Trautman JK. Near-field optics: microscopy, spectroscopy, and surface modification beyond the diffraction limit. Science. 1992;257:189–95. doi: 10.1126/science.257.5067.189. [DOI] [PubMed] [Google Scholar]
  • 11.Betzig E, Trautman JK, Wolfe R, Gyorgy EM, Finn PL, Kryder MH, Chang CH. Near-field magneto-optics and high density data storage. Appl Phys Lett. 1992;61:142–4. doi: 10.1063/1.108198. [DOI] [Google Scholar]
  • 12.Betzig E, Trautman JK, Weiner JS, Harris TD, Wolfe R. Polarization contrast in near-field scanning optical microscopy. Appl Opt. 1992;31:4563–8. doi: 10.1364/AO.31.004563. [DOI] [PubMed] [Google Scholar]
  • 13.Fumagalli P, Rosenberger A, Eggers G, Münnemann A, Held N, Günterodt G. Quantitative determination of the local Kerr rotation by scanning near-field magneto-optic microscopy. Appl Phys Lett. 1998;72:2803–5. doi: 10.1063/1.121463. [DOI] [Google Scholar]
  • 14.Kottler V, Essaidi N, Ronarch N, Chappert C, Chen Y. Dichroic imaging of magnetic domains with a scanning near-field optical microscope. J Magn Magn Mater. 1997;165:398–400. doi: 10.1016/S0304-8853(96)00568-9. [DOI] [Google Scholar]
  • 15.Mitsuoka Y, Nakajima K, Honma K, Chiba N, Muramatsu H, Ataka T, Sato K. Polarization properties of light emitted by a bent optical fiber probe and polarization contrast in scanning near-field optical microscopy. J Appl Phys. 1998;83:3998–4003. doi: 10.1063/1.367223. [DOI] [Google Scholar]
  • 16.Nakajima K, Mitsuoka Y, Chiba N, Muramatsu H, Ataka T, Sato K, Fujihira M. Polarization effect in scanning near-field optic/atomic-force microscopy (SNOM/AFM) Ultramicroscopy. 1998;71:257–62. doi: 10.1016/S0304-3991(97)00100-9. [DOI] [Google Scholar]
  • 17.Ishibashi T, Yoshida T, Iijima A, Sato K, Mitsuoka Y, Nakajima K. Polarization properties of bent‐type optical fibre probe for magneto‐optical imaging. J Microscopy. 1999;194:374–7. doi: 10.1046/j.1365-2818.1999.00506.x. [DOI] [PubMed] [Google Scholar]
  • 18.Ishibashi T, Yoshida T, Yamamoto J, Sato K, Mitsuoka Y, Nakajima K. Magneto-optical imaging by scanning near-field optical microscope using polarization modulation technique. J Magn Soc Jpn. 1999;23:712–4. doi: 10.3379/jmsjmag.23.712. [DOI] [Google Scholar]
  • 19.Yoshida T, Yamamoto J, Iijima A, Ishibashi T, Sato K, Nakajima K, Mitsuoka Y. Polarization properties of bent optical fiber probes and magneto-optical imaging in scanning near-field optical microscopy with the polarization modulation technique. J Magn Soc Jpn. 1999;23:1960–4. doi: 10.3379/jmsjmag.23.1960. [DOI] [Google Scholar]
  • 20.Schoenmaker J, Dantos AD, Souche Y, Seabra AC, Sampaio LC. Imaging of domain wall motion in small magnetic particles through near-field microscopy. Appl Phys Lett. 2006;88:062506. doi: 10.1063/1.2172016. [DOI] [Google Scholar]
  • 21.Schoenmaker J, Lancarotte MS, Seabra AC, Souche Y, Santos AD. Magnetic characterization of microscopic particles by MO‐SNOM. J Microscopy. 2004;214:22–6. doi: 10.1111/j.0022-2720.2004.01303.x. [DOI] [PubMed] [Google Scholar]
  • 22.Hecht B, Bielefeldt H, Inouye Y, Pohl DW, Nowotny L. Facts and artifacts in near-field optical microscopy. J Appl Phys. 1997;81:2492–8. doi: 10.1063/1.363956. [DOI] [Google Scholar]
  • 23.Hartschuh A, Qian H, Georgi C, Böhmler M, Novotny L. Tip-enhanced near-field optical microscopy of carbon nanotubes. Anal Bioanal Chem. 2009;394:1787–95. doi: 10.1007/s00216-009-2827-4. [DOI] [PubMed] [Google Scholar]
  • 24.Hartschuh A, Sánchez EJ, Xie XS, Novotny L. High-resolution near-field Raman microscopy of single-walled carbon nanotubes. Phys Rev Lett. 2003;90:095503. doi: 10.1103/PhysRevLett.90.095503. [DOI] [PubMed] [Google Scholar]
  • 25.Hartschuh A, Anderson N, Novotny L. Near‐field Raman spectroscopy using a sharp metal tip. J Microscopy. 2003;210:234–40. doi: 10.1046/j.1365-2818.2003.01137.x. [DOI] [PubMed] [Google Scholar]
  • 26.Hayazawa N, Yano T, Watanabe H, Inouye Y, Kawata K. Detection of an individual single-wall carbon nanotube by tip-enhanced near-field Raman spectroscopy. Chem Phys Lett. 2003;376:174–80. doi: 10.1016/S0009-2614(03)00883-2. [DOI] [Google Scholar]
  • 27.Zhang M, Wang J. Plasmonic lens focused longitudinal field excitation for tip-enhanced Raman spectroscopy. Nanoscale Res Lett. 2015;10:189. doi: 10.1186/s11671-015-0897-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 28.Aoyagi M, Niratisairak S, Sioda T, Ishibashi T. Extinction ratio in apertureless reflection-mode magneto-optical scanning near-field optical microscopy. IEEE Trans Magn. 2012;48:3670–2. doi: 10.1109/TMAG.2012.2202384. [DOI] [Google Scholar]
  • 29.Cai Y, Aoyagi M, Emoto A, Shioda T, Ishibashi T. Polarization state of scattered light in apertureless reflection-mode scanning near-field optical microscopy. J Magnetics. 2013;18:317–20. doi: 10.4283/JMAG.2013.18.3.317. [DOI] [Google Scholar]
  • 30.Cai Y, Meng Q, Emoto A, Shioda T, Ono H, Ishibashi T. FDTD analysis of polarization properties and backscattering coefficients in aperture-less SNOM. J Mag Soc Jpn. 2014;38:127–30. doi: 10.3379/msjmag.1403R004. [DOI] [Google Scholar]
  • 31.Walford JN, Porto JA, Carminati R, Greffet JJ. Theory of near-field magneto-optical imaging. J Opt Soc Am A. 2002;19:572–83. doi: 10.1364/JOSAA.19.000572. [DOI] [PubMed] [Google Scholar]
  • 32.Cai Y, Ikeda S, Nakagawa K, Kikuchi H, Shimidzu N, Ishibashi T. Strong enhancement of nano-sized circularly polarized light using an aperture antenna with V-groove structures. Opt Lett. 2015;40:1298–301. doi: 10.1364/OL.40.001298. [DOI] [PubMed] [Google Scholar]