. 2015 Nov 6;5:16272. doi: 10.1038/srep16272

Table 1. FWHM values (Δω and Δφ) of ω-, φ-scans, and % cube textures for the sample that includes Cu₂O (~0.5 μm)/SrTiO₃ (100 nm)/CeO₂ (60 nm)/YSZ (100 nm)/Y₂O₃ (80 nm)/Ni - 5 at% W (50 μm).

Layer (lattice parameter, a₀)	Δω (002 or 004)		Δφ (111)	%cube
Layer (lattice parameter, a₀)	(φ = 0°)	(φ = 90°)^*	Δφ (111)	%cube
Cu₂O (4.27 Å)	2.4°	4.7°	4.9°	98%
SrTiO₃ (3.91 Å)	2.8°	5.0°	5.4°	95%
CeO₂ (5.41 Å)	3.7°	6.4°	6.2°	97%
YSZ (5.15 Å)	3.9°	6.5°	6.1°	97%
Y₂O₃ (5.30 Å)	3.9°	6.5°	6.1°	94%
Ni - 5 at% W (3.52 Å)	5.2°	9.4°	6.3°	99%

^*φ = 0° and = 90° represent rolling and transverse directions of Ni-W tape, respectively.

Table 1. FWHM values (Δω and Δφ) of ω-, φ-scans, and % cube textures for the sample that includes Cu2O (~0.5 μm)/SrTiO3 (100 nm)/CeO2 (60 nm)/YSZ (100 nm)/Y2O3 (80 nm)/Ni - 5 at% W (50 μm).