Published in final edited form as: Ceram Int. 2016 Jan 1;42(1 Pt B):1077–1085. doi: 10.1016/j.ceramint.2015.09.033

Figure 2.

Figure 2

XRD patterns of three Y-TZP ceramics: High-Translucency, High-Strength and High-Surface Area. (a) Raw XRD spectral scans revealing major peaks of tetragonal, monoclinic, and cubic phases (20 to 80 degree). (b) XRD patterns in the region that consists of coexisting monoclinic and tetragonal phases (25 to 30 degree). Note: the curves were smoothed out to improve the resolution; (c) XRD patterns in the region that consists of coexisting cubic and tetragonal phases (72 to 76 degree). (d) XRD patterns of High-Strength bars fractured by the four-point bending test, with and without the simulated veneer firing treatment.