Figure 2.

Figure 2

(A) Dry-state stability testing of SAMT-10 at 70°C under a dry atmosphere for three months (N=3, mean ± SD). The percent recovery of the samples at 1 and 3 months was comparable to the control sample, which was stored at −20°C throughout the study period (p > 0.05, Student’s two-tailed t-test). (B) The percent recovery of SAMT-10 from the hydrophobic PEU when subjected to multiple extrusion cycles. There was no statistical significance observed in the percent recoveries between the three extrusion cycles (p = 0.28, one-way ANOVA).