Table 2. Fitted EIS parameters using the EEC model in Fig. 5 for uncoated and 3CHI3DCF- or 3CHI2DCF-coated AISI 316LVM stainless steel in physiological solution after 1 h, 3 h, 5 h, 7 h, and 10 h of immersion.

Immersion time [h]	χ2	RΩ	Q1	n1	R1	C1	Q2	n2	R2	C2	W
Uncoated sample
1	0.69	25.08	41.11	0.92	28.46	40.21	98.28	1.00	262.06	98.28	21.03
3	0.05	25.93	36.13	0.92	11.19	31.96	54.68	0.99	584.46	56.24	15.01
5	0.03	26.37	34.48	0.92	13.57	30.97	44.19	0.97	861.78	50.69	14.40
7	0.02	26.60	33.34	0.92	14.12	29.67	40.46	0.95	1116.14	49.53	13.68
10	0.02	26.82	32.13	0.92	15.04	28.68	38.26	0.94	1461.80	48.80	12.93
3CHI3DCF-coated sample
1	0.68	24.96	50.57	0.91	51.86	55.80	92.29	1.00	245.00	92.29	15.66
3	0.23	25.63	44.18	0.91	95.68	50.73	93.10	0.99	519.00	93.77	9.25
5	0.03	26.05	41.31	0.91	98.68	47.23	110.23	0.93	788.55	116.67	7.79
7	0.02	26.25	39.56	0.92	109.79	45.44	88.85	0.93	973.90	96.34	7.26
10	0.03	26.53	37.52	0.92	122.77	43.18	109.03	0.79	1475.50	840.05	7.17
3CHI2DCF-coated sample
1	0.52	25.14	41.31	0.89	23.49	40.54	71.00	1.00	351.30	71.00	15.60
3	0.22	25.96	34.51	0.89	28.50	34.11	56.45	1.00	716.40	56.45	10.89
5	0.23	26.42	32.31	0.89	30.85	32.10	54.81	0.93	1107.50	67.03	9.28
7	0.01	26.61	31.68	0.89	33.67	31.97	47.28	0.86	1370.00	70.62	11.10
10	0.26	26.89	29.69	0.89	47.29	30.83	42.12	0.74	2277.50	180.30	10.73

Units: χ² [×10⁻³], R_Ω [Ω cm²], R₁ and R₂ [kΩ cm²], Q₁ and Q₂ [μΩ⁻¹ cm⁻² sⁿ], W [μΩ⁻¹ cm⁻² s^1/2]; C [μF cm⁻²] was calculated as C_x = (R_xQ_x)n_x/R_x.