Table 2.

Minimum relative density	94 ± 1%
Electrical Resistivity at 300 K, ρ300	0.35–0.49 μΩm
Temperature Coefficient of Resistivity, αTCR	0.0035–0.0042 K−1
Decomposition/Melting Temperature	>1400 °C
Vickers Microindentation Hardness, HV	10.7 + 0.3 GPa
Thermal Expansion Coefficient, CTE	9.5 × 10−6 K−1
Thermal Conductivity at 300 K, κ	35.0 Wm−1K−1
Compressive Strength, σ+	1940 + 103 MPa
Compressive Strength, σ//	1418 + 281 MPa

Physical, thermal, and mechanical properties of hot-pressed MoAlB in this work.