Table 3. Rietveld quantitative phase analyses for the crystalline inorganic mixtures measured with Cu Kα1 and Mo Kα1 radiations.
Weighed amounts (%Wt) are shown for the sake of comparison (in bold). The AKLDs for each mixture and the KLD values for i-anhydrite are also included.
| CGpQ_0.0A | CGpQ_0.25A | CGpQ_0.50A | CGpQ_1.0A | CGpQ_2.0A | CGpQ_4.0A | |||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Phases | %Wt | Mo trm | Cu rfl | %Wt | Mo trm | Cu rfl | %Wt | Mo trm | Cu rfl | %Wt | Mo trm | Cu rfl | %Wt | Mo trm | Cu rfl | %Wt | Mo trm | Cu rfl |
| C | 32.9 | 32.6 (1) | 30.4 (2) | 32.8 | 32.0 (1) | 33.6 (1) | 32.7 | 33.2 (1) | 32.8 (1) | 32.5 | 32.8 (1) | 32.6 (2) | 32.2 | 31.3 (1) | 31.4 (1) | 31.6 | 31.2 (1) | 31.8 (1) |
| Gp | 31.7 | 31.7 (1) | 34.5 (1) | 31.7 | 32.5 (1) | 31.6 (1) | 31.6 | 30.1 (1) | 30.7 (1) | 31.5 | 30.4 (1) | 30.7 (1) | 31.1 | 32.1 (1) | 32.3 (1) | 30.5 | 30.7 (1) | 30.5 (1) |
| Q | 34.2 | 34.6 (1) | 33.7 (1) | 34.1 | 33.9 (1) | 33.0 (1) | 34.0 | 34.6 (1) | 34.2 (1) | 33.8 | 34.1 (1) | 33.8 (1) | 33.5 | 33.5 (1) | 32.6 (1) | 32.8 | 32.8 (1) | 32.0 (1) |
| s-A | 0.8 | 0.66 (3) | 0.76 (5) | 0.8 | 0.77 (4) | 0.78 (5) | 0.8 | 0.97 (3) | 1.15 (5) | 0.8 | 1.03 (4) | 1.11 (5) | 0.7 | 0.54 (3) | 0.58 (5) | 0.7 | 0.67 (3) | 0.77 (4) |
| SrSO4 | 0.4 | 0.44 (4) | 0.70 (6) | 0.4 | 0.44 (4) | 0.67 (5) | 0.4 | 0.39 (4) | 0.56 (5) | 0.4 | 0.43 (4) | 0.68 (5) | 0.4 | 0.48 (4) | 0.68 (6) | 0.4 | 0.45 (4) | 0.63 (5) |
| i-A | – | – | – | 0.28 | 0.42 (3) | 0.42 (4) | 0.52 | 0.71 (3) | 0.71 (4) | 1.02 | 1.23 (3) | 1.17 (5) | 2.02 | 2.05 (4) | 2.38 (9) | 4.02 | 4.30 (8) | 4.33 (9) |
| AKLD sum | 0.0089 | 0.0605 | 0.0198 | 0.0235 | 0.0295 | 0.0180 | 0.0214 | 0.0152 | 0.0218 | 0.0358 | 0.0095 | 0.0156 | ||||||
| (i-A) KLD | –0.001 | –0.001 | –0.002 | –0.002 | –0.002 | –0.001 | 0.000 | –0.003 | –0.004 | –0.003 | ||||||||