TABLE 2.

Frequency-Domain Intensity Decay of S101 in 290-nm-Thick PVA on a 50-nm Silver Film

observed angle	excitation polarization	observed polarization	〈τ〉 (ns)	τ̄(ns)	α1	f1	τ1 (ns)	α2	f2	τ2 (ns)	${\chi }_{\mathrm{R}}^2$
			Reverse Kretschmann Excitation
43.75°	H	p	2.34	3.19	0.317	0.038	0.28	0.683	0.962	3.30	1.0
	V	p	2.98	3.78	0.261	0.033	0.37	0.739	0.967	3.90	1.1
60°	V	s	2.32	3.44	0.380	0.043	0.27	0.620	0.957	3.58	1.4
	H	s	3.15	4.28	0.295	0.023	0.24	0.705	0.977	4.37	1.2
150°	V	p	2.82	3.48	0.233	0.028	0.34	0.767	0.972	3.57	0.9
	V	s	2.27	2.87	0.270	0.041	0.35	0.730	0.959	2.98	0.9
				Kretschmann Excitation
45.5°	H, 51.5°	p	2.72	3.50	0.268	0.032	0.33	0.732	0.968	3.60	0.9
45.2°	V, 64.3°	p	3.25	3.83	0.171	0.012	0.23	0.829	0.988	3.87	1.1
60°	H, 51.5°	s	3.26	3.97	0.200	0.014	0.23	0.800	0.986	4.02	0.9
59.7°	V, 64.3°	s	2.74	3.37	0.218	0.020	0.25	0.782	0.980	3.43	0.9