Table 2.

Danazol powder characteristics including percent degradation, particle sizing from DLS, D50 from MFI, BET surface area, and DSC melting temperature.

Sample	Degradation	Particle Size	NanoCluster D50 Size	BET Surface Area	DSC Melting Temperature
Stock Danazol	-	2.5 um*	2.5 um	3.28±0.03 m2/g	227.49 ºC
5 Hour Milled	0.39±0.20%	341.2±8.6 nm	2.0 um	25.86±0.10 m2/g	223.82 ºC
10 Hour Milled	0.90±0.48%	354.5±10.0 nm	1.8 um	36.75±0.14 m2/g	222.08 ºC
15 Hour Milled	1.23±0.06%	412.8±11.8 nm	1.6 um	47.65±0.26 m2/g	220.89 ºC
Nanoparticle Suspension	-	234.8±1.9 nm	-	34.07 m2/g**	224.78 ºC

^*Calculated from BET;

^**Calculated from particle size⁴⁵

Particle size was determined using DLS while MFI was used to determine NanoCluster D50 size.