. Author manuscript; available in PMC: 2016 Nov 1.

Published in final edited form as: Dent Mater. 2015 Sep 7;31(11):1255–1262. doi: 10.1016/j.dental.2015.08.148

Table 4.

Mechanical properties for the oligomeric thiol-ene and BisGMA/TEGDMA samples cured with 1 wt% IR 819, and 50 mW/cm² of 400–500 nm wavelength at ambient conditions. Standard deviations are given in parentheses. Values followed by the same letter in the same column are not significantly different.

Sample	Toughness (J·m⁻³·10⁴)	Young’s Modulus (GPa)	Flexural Strength (MPa)	Tg (°C)
BisGMA/TEGDMA	288 (129)^A	4.3 (0.2)^A	135 (22)^A	134 (1)^A
TEO 01	2566 (173)^B	3.4 (0.1)^D	110 (4)^B	73 (5)^B
TEO 02	690 (102)^C	2.8 (0.1)^B,C	99 (1)^B	89 (2)^C
TEO 03	470 (50)^A,C	2.6 (0.3)^B	92 (10)^B	79 (4)^B,C
TEO 04	512 (10)^C	3.1 (0.1)^C	104 (3)^B	81 (4)^B,C