Table 4. Summary of the Properties and DSC Results for LiBH4 Confined in Ordered Nanoporous Carbon Scaffolds.

sample LiBH4/wt % fraction confined/% Tonset, solid–solid/K ΔT solid–solid/K Tpeak ΔHsolid–solid/kJ/mol t/nm
Cm-0.8 30.8 82          
Cm-1.8 49.2 84 301 77 340 0.36 1.30
Cm-4.9 63.5 97 292 86 376 2.3 1.27