Table 2.

Tensile modulus and flatness error under different post-curing times.

▱ Flatness Error (mm)			Post-Curing Time (Minutes)
E Tensile Modulus (MPa)			0′	10′	20′	40′
Industrial Blend (no pigment)	Casting	▱ (mm)	0.75		1.23	1.78
		E (MPa)				511.1
Industrial Blend	MLL	▱ (mm)		0.19		0.2
		E (MPa)		609.1
Castable Blend	MLL	▱ (mm)		0.20
		E (MPa)		719.0
Castable Blend with support	Projet1200	▱ (mm)	0.3	1.7
		E (MPa)		651.2
Castable Blend no support	Projet 1200	▱ (mm)	0.14	0.14
		E (MPa)		911.6