Table 2. N2 Physisorption Characterization of Lewatit VP OC 1065 before and after Oxidative Degradation in Dry Air at 120°C for 72 h.

  fresh IER degraded IER
BET surface area (m2/g) 24.8 23.4
BJH pore volume (cm3/g) 0.20 0.16
BJH pore diameter (nm) 38 32