Published in final edited form as: Dent Mater. 2017 Mar 28;33(6):621–629. doi: 10.1016/j.dental.2017.03.010

Figure 2.

Figure 2

Polymerization kinetics of CuAAC composites (closed symbol) and BisGMA/TEGDMA composites (open symbol) with variable microfiller loadings including 0% (red square), 20% (orange circle), 40% (green triangle), and 60% (blue rhombus), as measured by FTIR. Each mixture was irradiated for 4 min at ambient temperature with 600 mW cm−2 of 400–500 nm light following 1 min in the dark to establish a baseline.