Table 2.

Tensile Test results: Tensile Modulus (E_t) Tensile Strength (σ_t) and Stress at break (σ_b).

Natural PLA
	1 ext			4 ext			8 ext
	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)
$\overline{x}$	3455.16	63.99	55.70	3557.98	65.17	54.86	3430.08	62.06	53.80
σ	105.06	1.02	1.39	169.26	0.76	1.91	40.98	0.84	1.53
n [%]	3.04	1.60	2.49	4.76	1.16	3.49	1.19	1.35	2.85
	12 ext			16 ext			20 ext
	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)
$\overline{x}$	3452.41	63.09	54.03	3411.64	59.07	53.55	3471.85	59.33	52.28
σ	42.92	2.10	2.56	55.22	1.74	4.43	66.44	1.77	1.81
n [%]	1.24	3.33	4.73	1.62	2.94	8.27	1.91	2.99	3.46
PLA BS
	1 ext			4 ext			8 ext
	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)
$\overline{x}$	3421.27	25.44	25.44	3309.94	61.02	51.40	3334.46	59.89	54.73
σ	108.31	3.42	3.42	74.18	1.59	5.54	119.11	0.33	1.05
n [%]	3.17	13.45	13.45	2.24	2.60	10.78	3.57	0.56	1.92
	12 ext			16 ext			20 ext
	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)
$\overline{x}$	3326.17	57.55	55.40	3362.31	59.90	53.04	3359.07	59.61	53.26
σ	50.97	0.51	2.87	0.07	1.04	0.90	70.55	0.78	1.03
n [%]	1.53	0.89	5.18	0.71	1.74	1.69	2.10	1.30	1.93
PLA Nano
	1 ext			4 ext			8 ext
	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)
$\overline{x}$	4137.82	33.10	33.10	4684.56	67.64	56.67	4742.92	41.16	1.53
σ	58.28	5.09	5.09	64.84	1.58	1.20	67.55	6.81	0.42
n [%]	1.41	15.37	15.37	1.38	2.33	2.12	1.42	16.54	27.78
	12 ext			16 ext			20 ext
	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)	Et (MPa)	σt (MPa)	σb (MPa)
$\overline{x}$	4966.33	64.50	64.50	4822.84	39.54	39.54	4890.39	57.36	2.48
σ	91.60	2.69	2.69	84.66	4.99	4.99	167.33	6.39	0.41
n [%]	1.84	4.17	4.17	1.76	12.63	12.63	3.42	11.14	16.68