. 2014 Dec 5;7(12):7799–7808. doi: 10.3390/ma7127799

Figure 3.

Figure 3

SEM fractograph of 316L tested in 30 wt. % MgCl2 at 150 °C, showing intergranularstress corrosion cracking (SCC) that covered a considerable fraction of the fracture surface, when tested at strain rates: (a) 3.7 × 10−7 s−1 and (b) 5.3 × 10−7 s−1.