. 2017 Jun 5;7(2):28. doi: 10.3390/membranes7020028

Table 2.

Time lag measurements at 30 °C of four gases using membranes formed by blending PIM-1 with different PEGs.

PEG-Content wt % d) Permeability (Barrer b)) Selectivity c)
N2 O2 CO2 CH4 O2/N2 CO2/N2 CO2/CH4
PIM-1 a) 0 360 1030 7160 590 2.8 19.9 12.1
+ PEG-200 6.2 115 310 2335 199 2.7 20.2 11.7
+ PEG-1000 5.3 120 361 2776 211 3.0 23.0 13.1
+ PEG-2000 5.0 100 314 2513 177 3.2 25.5 14.2
+ PEG-200 10.0 40 122 1097 78 3.0 26.8 14.1
+ PEG-1000 12.2 28 95 806 46 3.3 28.4 17.6
+ PEG-2000 11.0 20 74 660 37 3.5 30.9 18.0

a) Mw ca. 300 kg/mol (SEC/MALS detector); b) 1 × 10−10 (cm3(STP)cm cm−2 s−1cm Hg−1); c) Calculated from single gas measurements; d) Content of PEG as calculated from TGA.