Table 2.
Differential scanning calorimetry parameters of isothermally crystallized samples.
| Samples | First Melting | Second Melting | Cooling | ||
|---|---|---|---|---|---|
| Tm (°C) | Xc (%) | Tm (°C) | Xc (%) | Tc (°C) | |
| Neat PLA | 165.9, 171.7 | 20.87 | 165.3, 170.2 | 15.24 | - |
| PLA/PF (90/10) | 165.0, 170.8 | 41.67 | 166.6, 170.8 | 40.19 | 112.7 |
| PLA/PF (80/20) | 165.8, 171.0 | 49.86 | 166.9, 170.5 | 47.84 | 122.3 |
| PLA/PF (70/30) | 163.0, 170.0 | 45.36 | 166.5, 170.2 | 44.23 | 118.5 |
| PLA/PF (60/40) | 165.9, 171.9 | 44.28 | 165.9, 171.2 | 43.86 | 112.3 |
| PLA/T-PF (90/10) | 166.2, 171.6 | 40.17 | 165.5, 170.8 | 40.01 | 109.2 |
| PLA/T-PF (80/20) | 165.1, 170.9 | 47.28 | 164.5, 170.5 | 45.36 | 112.3 |
| PLA/T-PF (70/30) | 164.3, 170.0 | 43.76 | 164.2, 170.0 | 42.94 | 111.5 |
| PLA/T-PF (60/40) | 164.2, 170.7 | 42.15 | 165.2, 169.7 | 40.73 | 107.5 |
| PLA/PBAT/T-PF (60/10/30) | 166.1, 171.5 | 35.69 | 163.3, 170.8 | 32.15 | 100.4 |
| PLA/PBAT/T-PF (50/20/30) | 163.1, 170.1 | 30.75 | 168.6 | 28.85 | 96.6 |