Table 2.
Descriptive statistics with mean and standard deviation (SD) of weight analysis (water absorption) of tested SACRCs for each storage medium and aging level in alphabetical order, respectively.
| Material | 0d | 7d | 28d | 90d | 180d | 365d |
|---|---|---|---|---|---|---|
| Distilled water | ||||||
| BEA | 0.337 ± 0.008 | 0.342 ± 0.007 | 0.346 ± 0.007 | 0.347 ± 0.007 | 0.348 ± 0.007 | 0.348 ± 0.007 |
| BIF | 0.366 ± 0.011 | 0.368 ± 0.011 | 0.375 ± 0.011 | 0.375 ± 0.011 | 0.376 ± 0.011 | 0.375 ± 0.011 |
| CLE | 0.353 ± 0.011 | 0.357 ± 0.011 | 0.358 ± 0.011 | 0.360 ± 0.011 | 0.360 ± 0.011 | 0.361 ± 0.011 |
| RXU | * 0.357 ± 0.008 | * 0.363 ± 0.008 | * 0.364 ± 0.008 | * 0.367 ± 0.008 | * 0.368 ± 0.008 | 0.367 ± 0.008 |
| SET | 0.356 ± 0.012 | 0.368 ± 0.013 | 0.368 ± 0.013 | 0.369 ± 0.013 | 0.369 ± 0.013 | 0.369 ± 0.012 |
| SMC | 0.388 ± 0.011 | 0.394 ± 0.011 | 0.396 ± 0.011 | 0.396 ± 0.011 | 0.395 ± 0.011 | 0.395 ± 0.011 |
| SOC | 0.431 ± 0.013 | 0.439 ± 0.014 | 0.441 ± 0.014 | 0.442 ± 0.014 | 0.443 ± 0.014 | 0.443 ± 0.014 |
| SPC | 0.411 ± 0.015 | 0.416 ± 0.015 | 0.417 ± 0.015 | 0.417 ± 0.015 | 0.417 ± 0.015 | 0.417 ± 0.015 |
| Red wine | ||||||
| BEA | 0.334 ± 0.011 | 0.339 ± 0.010 | 0.342 ± 0.010 | 0.344 ± 0.010 | 0.345 ± 0.011 | 0.351 ± 0.011 |
| BIF | 0.368 ± 0.012 | 0.371 ± 0.012 | 0.376 ± 0.013 | 0.378 ± 0.012 | 0.378 ± 0.012 | 0.394 ± 0.015 |
| CLE | 0.357 ± 0.009 | 0.361 ± 0.009 | 0.361 ± 0.010 | 0.365 ± 0.009 | 0.367 ± 0.100 | 0.373 ± 0.011 |
| RXU | 0.359 ± 0.008 | 0.363 ± 0.008 | 0.365 ± 0.008 | 0.367 ± 0.008 | 0.369 ± 0.007 | 0.382 ± 0.013 |
| SET | * 0.350 ± 0.016 | 0.361 ± 0.016 | * 0.362 ± 0.016 | 0.362 ± 0.016 | 0.360 ± 0.015 | 0.363 ± 0.016 |
| SMC | 0.383 ± 0.008 | 0.391 ± 0.008 | 0.392 ± 0.008 | 0.393 ± 0.008 | 0.394 ± 0.008 | 0.406 ± 0.013 |
| SOC | 0.440 ± 0.016 | 0.447 ± 0.016 | 0.450 ± 0.0160 | 0.451 ± 0.016 | 0.452 ± 0.016 | * 0.467 ± 0.025 |
| SPC | 0.412 ± 0.016 | 0.417 ± 0.016 | 0.417 ± 0.016 | 0.419 ± 0.016 | 0.423 ± 0.016 | 0.433 ± 0.016 |
| Curry solution | ||||||
| BEA | 0.337 ± 0.009 | 0.342 ± 0.009 | 0.346 ± 0.010 | 0.347 ± 0.010 | 0.347 ± 0.010 | 0.347 ± 0.010 |
| BIF | 0.370 ± 0.010 | * 0.371 ± 0.010 | 0.379 ± 0.010 | * 0.380 ± 0.011 | * 0.380 ± 0.010 | * 0.380 ± 0.011 |
| CLE | 0.358 ± 0.007 | 0.362 ± 0.007 | * 0.364 ± 0.008 | * 0.367 ± 0.007 | * 0.367 ± 0.007 | * 0.367 ± 0.007 |
| RXU | 0.358 ± 0.009 | 0.362 ± 0.009 | 0.367 ± 0.009 | 0.368 ± 0.009 | 0.368 ± 0.009 | 0.369 ± 0.009 |
| SET | 0.357 ± 0.009 | 0.369 ± 0.010 | 0.370 ± 0.01 | 0.370 ± 0.010 | 0.369 ± 0.010 | 0.369 ± 0.010 |
| SMC | 0.388 ± 0.012 | 0.394 ± 0.012 | 0.394 ± 0.012 | 0.394 ± 0.012 | 0.393 ± 0.012 | 0.393 ± 0.012 |
| SOC | 0.443 ± 0.018 | 0.450 ± 0.018 | 0.452 ± 0.019 | 0.453 ± 0.019 | 0.454 ± 0.019 | 0.454 ± 0.018 |
| SPC | 0.410 ± 0.017 | 0.416 ± 0.017 | 0.416 ± 0.017 | 0.417 ± 0.017 | 0.416 ± 0.017 | 0.418 ± 0.016 |
| Cress solution | ||||||
| BEA | 0.332 ± 0.008 | 0.338 ± 0.008 | 0.342 ± 0.008 | 0.342 ± 0.008 | 0.343 ± 0.008 | 0.344 ± 0.008 |
| BIF | 0.367 ± 0.010 | 0.370 ± 0.010 | 0.376 ± 0.011 | 0.376 ± 0.010 | 0.376 ± 0.010 | 0.377 ± 0.010 |
| CLE | 0.355 ± 0.009 | 0.360 ± 0.009 | 0.361 ± 0.010 | 0.362 ± 0.010 | 0.363 ± 0.009 | 0.364 ± 0.010 |
| RXU | 0.356 ± 0.007 | 0.360 ± 0.007 | 0.365 ± 0.008 | 0.366 ± 0.007 | 0.366 ± 0.007 | 0.369 ± 0.006 |
| SET | 0.360 ± 0.009 | 0.371 ± 0.010 | 0.371 ± 0.010 | 0.370 ± 0.010 | 0.370 ± 0.010 | 0.371 ± 0.010 |
| SMC | 0.390 ± 0.009 | 0.395 ± 0.004 | 0.395 ± 0.009 | 0.395 ± 0.009 | 0.395 ± 0.009 | 0.395 ± 0.009 |
| SOC | 0.448 ± 0.015 | 0.455 ± 0.015 | 0.456 ± 0.015 | 0.457 ± 0.015 | 0.458 ± 0.015 | 0.459 ± 0.015 |
| SPC | 0.408 ± 0.015 | 0.414 ± 0.015 | 0.414 ± 0.015 | 0.414 ± 0.015 | 0.414 ± 0.015 | 0.414 ± 0.015 |
* not normally distributed.