Published in final edited form as: Nanoscale. 2017 Sep 21;9(36):13465–13476. doi: 10.1039/c7nr02363d

Figure 1. Differential scanning calorimetry of the PEG(2k)-b-TCL(11.2k) copolymer.

Figure 1

The sample was heated between −80 and +80C at 5 °C/min ramp. (A) Plot of its phase transitions as a function of temperature. (B) Table of major transitions seen in repeated heating cycles. Tg: glass transition temperature, Tc: crystallization temperature, Tm: melting temperature.