Table 3. Photophysical Properties of the Copolymers Measured as Thin Films Prepared from Toluene or DCB (λ_absmax, Absorption Maximum; λ_PLmax, Emission Maximum; λ_PLexcmax, Maximum of the Excitation Spectrum; d, Film Thickness; Primary Maxima in Bold).

thin film	prepared from	d (nm)	λabsmax (nm)	λPLmaxa (nm)	λPLexcmaxb (nm)
P1	DCB	10	213, 304, 427, 604	–	–
P2	DCB	46	212, 286, 557, 591	625	488, 531, 571
P2	DCB	87	212, 286, 547, 581	625	487, 529, 570
P2	toluene	52	213, 336, 488, 590	621	333, 457, 486, 523, 577
P2	toluene	157	212, 336, 484, 584	623	336, 458, 484, 525, 589
P3	DCB	47	213, 337, 483	609	335, 454, 485
P3	DCB	70	213, 335, 479	604	331, 451, 482
P3	toluene	30	214, 337, 484	605	335, 454, 485
P3	toluene	111	213, 334, 462	611	334, 456, 485
SM	DCB	43	206, 231, 258, 342, 423, 455 sh, 525 sh	567	339, 421

^aExcitation wavelength at λ_absmax;

^bEmission wavelength at λ_PLmax