Published in final edited form as: J Polym Sci A Polym Chem. 2017 Mar 25;55(12):2019–2026. doi: 10.1002/pola.28579

Figure 6. a) Storage modulus (E’) as a function of temperature and b) tan δ as a function of temperature for RT-0.6 non-degraded gel and gel degraded in ethanol.

Figure 6

A decrease in rubbery modulus is seen due to decreased crosslink density caused by degradation.