Table 1. Thermo-mechanical and thermal-stability results.

Sample	T_g ^a (°C)	Weight loss (°C)			T_max ^e	Residual mass (600 °C) (%)
Sample	T_g ^a (°C)	T_d 5% ^b	T_d 50% ^c	T_d 90% ^d	T_max ^e	Residual mass (600 °C) (%)
ECO	45	162	355	423	368	1.2
ECO_POSS1Ep	51	272	369	422	382	1.7
ECO_POSS8Ep	64	299	384	446	391	3.0

^{^a}

T _g – the maximum of tan δ plots was considered for the glass transition temperature (T _g) determination.

^{^b}

T _d 5% – temperature at which the mass loss of the sample is 5%.

^{^c}

T _d 50% – temperature at which the mass loss of the sample is 50%.

^{^d}

T _d 90% – temperature at which the mass loss of the sample is 90%.

^{^e}

T _max – temperature at which the weight loss is maximum.