. 2018 Apr 30;8:6780. doi: 10.1038/s41598-018-24671-x

Figure 4.

Figure 4

(a) SEM images of AFM tip interaction with 2% PDMS highlighting the adhesion between PDMS and Silicon Nitride AFM Tip snapping into and coming out of contact as indicated by the arrow. Scale bar is 100 um and (b) Nanoindentation by AFM retraction (lift) curves for PDMS samples tested wet in ethanol solution. All AFM experiments were conducted with an indentation depth of between 500 and 1000 nm and each curve was done over 1 s, each sample was tested in three different locations and 3 samples tested per formulation giving 900 data points per formulation (c) the average adhesion strength and peak adhesive force obtained by wet AFM.