. 2018 Jun 7;11(6):967. doi: 10.3390/ma11060967

Figure 1.

Figure 1

Figure 1

As cast alloy CM1 (a) CM1-10g button, (b) CM1-6mm (bulk) and (ce) CM1-8mm suctions cast bars, (c) bulk, (d) and (e) from area of high cooling rate and 18.6 < Si < 19.2 at.%. Rectangles show lamellar microstructures. The lamellar microstructure resulting from the eutectoid transformation of Nb3Si is shown in the right hand side of (e).