Table 1.
The composition of resin cements.
| Material | Type | Composition | Curing Time (s) | Manufacturer |
|---|---|---|---|---|
| Cement-It | Composite resin cement | bis-GMA, UDMA, HDDMA, PEGDMA, barium-boro-silicate glass (65 wt %) | 20 | Jeneric Pentron (Wallingford, CT, USA) |
| NX3 | Composite resin cement | TEGDMA, bis-GMA, fluoro-aluminosilicate glass (67.5 wt %/47 vol %), activators, stabilizers, radiopaque agent | 20 | Kerr (Orange, CA, USA) |
| Variolink Esthetic DC | Composite resin cement | UMDA and further methacrylate monomers, ytterbium trifluoride, spheroid mixed oxide (67 wt %/38 vol %), initiators, stabilizers and pigments | 10 | Ivoclar Vivadent (Ellwangen, Germany) |
| Estecem | Adhesive resin cement | bis-GMA, TEGDMA, bis-MPEPP, silica-zirconia filler (74 wt %), camphorquinone | 20 | Tokuyama Dental (Taitou, Japan) |
| Multilink Automix | Adhesive resin cement | dimethacrylate and HEMA, barium glass and silica filler, ytterbiumtrifluoride (68 wt %), catalysts, stabilizers, pigments | 10 | Ivoclar Vivadent (Ellwangen, Germany) |
| Panavia 2.0 | Adhesive resin cement | 10-MDP, BPEDMA, hydrophobic aliphatic metahrylates, hydrophilic aliphatic metahrylate, silanated silica filler, silanated barium glass filler, sodium fluoride (70.8 wt %) | 20 | Kuraray (Osaka, Japan) |
| Breeze | Self-adhesive resin cement | bis-GMA, UDMA, TEGDMA, HEMA, 4-MET, silane treated barium glass, silica, BiOCl, Ca-Al-F-silicate, curing system | 20 | Jeneric Pentron (Wallingford, CT, USA) |
| Calibra Universal | Self-adhesive resin cement | UDMA, trimethylolpropane trimethacrylate TMPTMA, bis-EMA—Bisphenol A ethoxylate dimethacrylate, TEGDMA, HEMA, 3-(acryloyloxy)-2-hydroxypropyl methacrylate, urethane modified bis-GMA, PENTA, silanated barium glass, fumed silica (48 vol %) | 10 | Dentsply Sirona (York, PA, USA) |
| MaxCem Elite Chroma | Self-adhesive resin cement | HEMA, GDM, UDMA, 1,1,3,3-tetramethylbutyl hydroperoxide TEGDMA, fluoroaluminosilicate glass, GPDM, barium glass filler, fumed silica (69 wt %) | 10 | Kerr (Orange, CA, USA) |
| Panavia SA Cement Plus | Self-adhesive resin cement | bis-GMA, TEGDMA, HEMA, 10-MDP, hydrophobic aromatic dimethacrylate, hydrophobic aliphatic dimethacrylate, sodium fluoride, silanated barium glass filler, silanated colloidal silica (70 wt %/40 vol %) | 10 | Kuraray (Osaka, Japan) |
| RelyX U200 | Self-adhesive resin cement | methacrylate monomers containing phosphoric acid groups, methacrylate monomers, silanated fillers (70 wt %/43 vol %), initiator components, stabilizers, rheological additives, alkaline(basic) initiator components, stabilizers, pigments | 20 | 3M ESPE (St. Paul, MN, USA) |
| SmartCem 2 | Self-adhesive resin cement | UDMA, urethane modified bis-GMA, TEGDMA, PENTA, dimethacrylate resins, barium boron fluoroaluminosilicate glass amorphous silica (69 wt %/46 vol %) | 10 | Dentsply Sirona (York, PA, USA) |
| SpeedCEM Plus | Self-adhesive resin cement | UDMA, TEGDMA, PEGDMA, methacrylated phosphoric acid ester, 1,10-decandiol dimethacrylate, copolymers, dibenzoyl peroxide, ytterbium trifluoride, barium glass, silicon dioxide (75 wt %/45 vol %) | 20 | Ivoclar Vivadent (Ellwangen, Germany) |
bis-GMA—bisphenol A glycol dimethacrylate, UDMA—urethane dimethacrylate , TEGDMA—triethylene glycol dimethacrylate, GDM—glycerol 1,3-dimethacrylate, GPDM—glycerol phosphate dimethacryalte, bis-MPEPP—bisphenol A polyethoxy methacrylate, HEMA—hydroxyethyl methacrylate, PEGDMA—polyethylene glycol dimethacrylate, NPGDMA—neopentyldimethacrylate, 10-MDP—10-methacryloxydecyl dihydrogen phosphate, BPEDMA—bisphenol-A-polyethoxy dimethacrylate, PENTA—dipentaerythritol penttacrylate monophosphate, HDDMA—1,6-hexanediol dimethacrylate, 4-MET—4-methacryloyloxyethy trimellitate anhydride, MAC-10—11-methacryloyloxy-1,1-undecanedicarboxylic acid, TMPTMA—trimethylolpropane trimethacrylate.