Table 3.
Geometrical details of materials investigated and operational characteristics during MLLDP analysis.
| Materials | Shape | Geometry | Nominal Pore Size | Liquid System (B/A) | Δp (bar) | Test Rig |
|---|---|---|---|---|---|---|
| AnoporeTM membrane | Planar | O.d.: 7 mm Thickness: 60 μm |
100 nm | Isobutyl alcohol/water | 0.4–1.0 | Figure 3 |
| PVDF membrane | Tubular | O.d.: 1.2 mm I.d.: 0.7 mmL: 40 cm |
80 nm | Isobutyl alcohol/water | 0.4–1.0 | Figure 4 |
| ZrO2/γ-Al2O3/α-Al2O3 membrane | Single tubular | O.d.: 13 mm I.d.: 11 mmL: 5 cm |
30 nm | Isobutyl alcohol/water | 0.6–3.0 | Figure 4 |
| ZrO2/γ-Al2O3/α-Al2O3 membrane | Multi-channel tubular | O.d.: 32 mm Channel i.d.: 4 mmL: 100 cmChannel no.: 19 |
100 nm | n-amyl alcohol/water | 0.4–2.8 | Figure 5 |
| Defects of Pd/ZrO2/Al2O3 membrane | Tubular | O.d.: 13 mm I.d.: 11 mmL: 5 cm |
- | Isobutyl alcohol/water | 0.32–3.0 | Figure 4 |