. 2018 May 14;19(7):2969–2978. doi: 10.1021/acs.biomac.8b00536

Table 3. Mechanical Properties of DAC and All-Cellulose DAC/CNC Composite Films of Different Water Contents under Tensile Stress (n = 4): Modulus of Elasticity (E_mod), Ultimate Strength (UTS), Elongation at Break (dL at F_max), and Toughness (U_T).

H₂O [wt %]	CNC [wt %]	E_mod [GPa]	UTS (σ_M) [MPa]	dL at F_max [%]	U_T [J m^–3·10⁴]
1	0	3.41 ± 0.16	122.46 ± 4.96	7.23 ± 1.06	603.20 ± 137.89
6	0	4.03 ± 0.09	80.92 ± 8.09	2.24 ± 0.34	103.33 ± 25.31
7	5	4.70 ± 0.23	120.91 ± 3.00	2.82 ± 0.21	172.68 ± 21.04

Table 3. Mechanical Properties of DAC and All-Cellulose DAC/CNC Composite Films of Different Water Contents under Tensile Stress (n = 4): Modulus of Elasticity (Emod), Ultimate Strength (UTS), Elongation at Break (dL at Fmax), and Toughness (UT).