. 2018 Jul 30;9:2942. doi: 10.1038/s41467-018-05289-z

Table 1.

Correlation between the local Li growth rate and Li⁺ concentration heterogeneity

			No depletion (35/40 min)	Partial depletion (65/70 min)	Full depletion (100/105 min)
Experimental results	v (μm min^–1)		0.20 ± 0.18	1.14 ± 0.96	1.62 ± 1.23
	[Li⁺]_10 μm (mM)	t1	91 ± 23	55 ± 21	50 ± 30
	[Li⁺]_10 μm (mM)	t2	86 ± 24	37 ± 21	48 ± 31
	R of v and [Li⁺]_10 μm in Fig. 4	t1	0.05	0.22	0.58
	R of v and [Li⁺]_10 μm in Fig. 4	t2	0.29	0.59	0.84
Simulation results	v (μm min^–1)		0.25 ± 0.30	0.42 ± 0.45	0.86 ± 0.82
	[Li⁺]_10 μm (mM)	t1	/	/	/
	[Li⁺]_10 μm (mM)	t2	81 ± 17	57 ± 19	46 ± 26
	R of v and [Li⁺]_10 μm in Supplementary Fig. 13	t1	0.30	0.48	0.78
	R of v and [Li⁺]_10 μm in Supplementary Fig. 13	t2	0.45	0.73	0.86