Table 1. Comparison of experimental and calculated distances and angles (Å, °) in 1 and 2 .

1
Ni1—O1	2.0622 (14)	2.07
Ni1—O1W	2.0831 (15)	2.10
Ni1—N1	2.1019 (14)	2.12
O2—N2	1.2520 (14)	1.23
O3—N2	1.2548 (12)	1.22
O4—N2	1.2537 (12)	1.27
O1—Ni1—O1W	90.74 (4)	93.00
O1—Ni1—N1	88.68 (3)	87.00
O1—Ni1—O1W i	89.26 (4)	91.8
O1—Ni1—N1i	91.32 (3)	92.3
O1W—Ni1—N1	90.00 (4)	92
O1i—Ni1—O1W	89.26 (4)	87.00
O1W—Ni1—N1i	90.00 (4)	91.8
O1i—Ni1—N1	91.32 (3)	92.3
O1W i—Ni1—N1	90.00 (4)	91.8
O1i—Ni1—O1W i	90.74 (4)	87.5
O1W—Ni1—O1—C2	−79.99 (10)	80.02
N1i—Ni1—O1—C2	−170.01 (10)	166.70
O1—Ni1—N1—C4	−29.33 (10)	31.30
O1—Ni1—N1—C8	151.96 (9)	−147.60
O1W i—Ni1—N1—C4	−118.59 (9)	114.9
O1W i—Ni1—N1—C8	62.70 (9)	−64.00
2
Cu1—O1	2.01	2.08
Cu1—N1	2.02	1.99
Cu1—O1i	2.01	2.08
Cu1—N1i	2.02	1.99
Cu2—O2	2.05	2.08
N2—Cu2—N2ii	180	180.00
O1—Cu1—N1	92.39	90.60
O1—Cu1—O1i	180	180.00
O3—Cu1—O1—C1	−93.9	−98
O1—Cu1—N1—C7	−151.03	−153
N2—Cu2—O2—C8	151.24	148
Cu1—O1—C1—C2	−37.55.	−40
C7—N1—C3—C2	177	179
C7—N1—C3—C4	−0.5	−0.4