Table 1.

Measured δ and calculated m values as a function of deformation temperature and strain rate in Ti-6Al-4V alloy.

Temperature T, (K)	Initial Strain Rate $\dot{\mathit{\epsilon }}$, (s−1)	Strain Rate Sensitivity Exponent m	Elongation to Failure δ, (%)
1123	5 × 10−3	0.39	263
1123	10−3	0.52	758
1123	5 × 10−4	0.52	768
1073	5 × 10−3	0.38	240
1073	10−3	0.46	466
1073	5 × 10−4	0.48	536
1023	5 × 10−3	0.39	256
1023	10−3	0.43	347
1023	5 × 10−4	0.45	406
973	5 × 10−3	0.23	82
973	10−3	0.39	252
973	5 × 10−4	0.43	366
973	3 × 10−4	0.43	359