Table 1.

Mono-aromatic, di-epoxy monomers and thermal properties of the cured materials. T_g values are indicated in plain text, T_α are in italics.

Epoxy	Curing Agent	Tg (°C) or Tα (°C)		Td,5% (°C)	Reference
		Materials	DGEBA Comparison
	2,5-difluoroterephthalic acid	69	66	242	[154]
	2,5-difluoroterephthalic acid	74	66	305
	Diethyl toluene diamine EPIKURE W	193 a	185 a/198 b	-	[150]
	4,4′-methylene biscyclohexylamine PACM	100 a/111 b	167 a/176 b	-
	Diethyl toluene diamine EPIKURE W	132 a/140 b	185 a/198 b	-
	Methyhexahydrophthalic anhydride MHHPA	129 b	125	284	[132]
	Poly(propylene glycol) bis(2-aminopropyl ether) D230	92 b	97	266
	4,4′-methylenebiscyclohexylamine	100 a/107 b	149 a/158 b	341	[17]
	Isophorone Diamine	97/106 b	166/182 b	361 c	[27,135]
	Isophorone Diamine	152/166 b	166/182 b	315 c
	Isophorone Diamine	132/154 b	166/182 b	328
	Bisfurfurylamine A	85	111	312	[148]
	Vanillylamine	64	67	262
	1,10-diaminodecane	74	98	328
	Hexahydrophthalic anhydride	114	106	321	[119]
	Maleopimaric acid	155	-	317
	1,2-cyclohexanedicarboxylic anhydride	154	144	311	[139]

^a T_α measured by DMA at the peak position of loss modulus curve; ^b T_α measured by DMA at the maximum of tan δ; ^c T_d,50%.