Table 2. Mechanical properties obtained from the uniaxial tests of the MEO₂MA elastomers prepared with different amounts of HPR-C as a cross-linker.

	0.5 wt % HPR-C	1.0 wt % HPR-C	2.0 wt % HPR-C	4.0 wt % HPR-C
Young’s modulus E (kPa)	125	280	349	400
Extension at break λ (mm/mm)	760	620	615	481
U (kPa)	70.8	102.2	138.3	145.9
Γ (J/m2)	415.9	703.1	1019.1	1320.2