Abstract
Rare-earth substituted inorganic phosphors are critical for solid state lighting. New phosphors are traditionally identified through chemical intuition or trial and error synthesis, inhibiting the discovery of potential high-performance materials. Here, we merge a support vector machine regression model to predict a phosphor host crystal structure’s Debye temperature, which is a proxy for photoluminescent quantum yield, with high-throughput density functional theory calculations to evaluate the band gap. This platform allows the identification of phosphors that may have otherwise been overlooked. Among the compounds with the highest Debye temperature and largest band gap, NaBaB9O15 shows outstanding potential. Following its synthesis and structural characterization, the structural rigidity is confirmed to stem from a unique corner sharing [B3O7]5– polyanionic backbone. Substituting this material with Eu2+ yields UV excitation bands and a narrow violet emission at 416 nm with a full-width at half-maximum of 34.5 nm. More importantly, NaBaB9O15:Eu2+ possesses a quantum yield of 95% and excellent thermal stability.
Identifying phosphors with good thermal stability and quantum efficiency is a prerequisite to improve the performance of white LED light sources. Here, a combined machine learning and density functional theory method is introduced to identify next generation inorganic phosphors.
Introduction
Inorganic phosphors are among the most significant components in a light-emitting diode (LED)-based white light and greatly influence the device’s overall efficacy1–3. These materials are composed of a host crystal structure, often an oxide, halide, or nitride, that are substituted with a rare-earth luminescent center, typically Eu2+ or Ce3+4–7. The rare-earth ion absorbs at least part of the LED emission and then re-emits a photon at a longer wavelength. The combination of these emissive lights cover the entire visible portion of the electromagnetic spectrum and thus appears as white light3,8. The efficiency, color quality, and compact size make these devices not only useful for general illumination, but they are also essential for modern display applications9. Unfortunately, only a handful of the phosphors currently reported in the literature are able to perform the down-conversion process efficiently, as measured by the photoluminescent quantum yield (Φ)10. Even then, some of the phosphors with a high luminescence quantum efficiency also suffer from thermal quenching, where the optical properties, for example, emission wavelength and intensity, change at elevated temperature limiting their range of potential applications11–15. Therefore, the continued improvement of LED-based lighting requires the discovery of new efficient and thermally robust rare-earth substituted inorganic phosphors.
In the search for new phosphors, research has shown one viable method for identifying materials with a high Φ is to find structurally rigid host compounds with high atomic connectivity16. These characteristics enhance Φ by inhibiting soft phonon modes that lead to non-radiative relaxation, thereby increasing the propensity for photon emission. However, the complex nature of chemical bonding in inorganic solids makes clearly identifying connectivity and structural rigidity challenging, and the comparison of rigidity between multiple solids problematic. Alternatively, it is possible to use a proxy, which is a quantifiable metric that scales with structural rigidity, to compare different materials. Prior work has already shown that a material’s Debye temperature (ΘD) is the most reliable proxy for structural rigidity, and consequently useful for screening Φ17–19. Materials with a higher ΘD tend to have higher-energy phonon modes that decrease the probability of non-radiative relaxation increasing Φ, whereas materials with a low ΘD tend to contain softer phonon modes that can promote non-radiative relaxation. More importantly, ΘD can be estimated using density functional theory (DFT), allowing for the potential of high-throughput screening20. Nevertheless, this approach has numerous drawbacks; most notably, calculating ΘD using DFT is computationally arduous. DFT cannot easily account for atomic disorder like site sharing which is common in complex inorganic solids, and it is currently restricted to smaller unit cells, typically a few hundred atoms at most. These limitations have permitted the elastic moduli, which are necessary to estimate ΘD, to be calculated for only a few thousand compounds, or <10% of the reported inorganic solids.
Advances in machine learning provides an avenue to significantly expand the physical and mechanical properties of inorganic solids and can push materials development beyond the current capability of DFT alone21,22. For example, it is possible to use a kernel ridge regression model to predict a myriad of electronic properties including dielectric constants, electron affinities, formation energies, and even band gaps23,24. A more intricate method employing a gradient boosting decision tree and universal fragment descriptors is able to predict the electronic as well as mechanical properties, such as bulk and shear modulus, heat capacity, and Debye temperature25. Machine learning has also allowed researchers to predict glass formation26, study magnetoelectric heterostructures27, and optimize microstructure28,29. The great advantage of using statistical machine-learning methods is that predictions can be quickly made for any given combination of elements, any stoichiometry, or any size unit cell. We show here that it is also possible to use machine learning to predict ΘD for a majority of compounds in the Pearson’s crystal database (PCD)30 in seconds regardless of unit cell size, atomic mixing, or electron correlation resulting in ~120,000 Debye temperatures that can be used for screening inorganic phosphors.
Knowledge of a crystal structure’s ΘD alone is still not sufficient to produce a high photoluminescence quantum efficiency inorganic phosphor. A wide band gap (Eg) in the host crystal structure is also crucial20. The size of the band gap sets the relative position of the rare-earth 5d orbitals with respect to the host crystal’s conduction band, which can influence the optical response. If the band gap of the host is small, the excited-state 5d orbitals may be close enough to the conduction band of the host crystal structure to allow (temperature-induced) photoionization or charge transfer. These non-radiative processes can both greatly diminish Φ31,32. Therefore, it is essential to ensure that any potential host also has a suitable band gap when screening for new phosphors. These two properties can ultimately be optimized by plotting ΘD as a function of DFT calculated Eg, which serves as a sorting diagram. For example, phosphors hosts that fall in the bottom-left corner of this sorting diagram have a low ΘD and a narrow Eg, suggesting that they are likely not worth immediate exploration, whereas compounds in the top-right corner of this plot are not only structurally rigid but also have a wide enough band gap to support rare-earth luminescence20. The success of this initial sorting diagram has already supported the discovery of numerous inorganic phosphors5.
This work establishes a new approach for phosphor screening methods by constructing a more extensive sorting diagram that merges supervised machine learning to predict ΘD with high-throughput calculations using DFT for approximating band gap (Eg,DFT). These scalable methods increase the number of potential phosphor hosts contained on the new sorting diagram 50-fold compared to the original approach; therefore, functioning as a more robust guide for phosphor development. Here we use this approach to identify one specific crystal structure that stands out among the 2071 materials on our sorting diagram. NaBaB9O15 has a high predicted Debye temperature of 729 K, surprising given the mostly ionic bonding and low-density crystal structure, as well as a wide Eg,DFT of 5.5 eV, making it worthy of experimental investigation. The subsequent synthesis of NaBaB9O15 substituted with Eu2+ indicates that this compound not only has a Φ near unity but also shows minimal thermal quenching. These results substantiate the effectiveness of using this sorting diagram to direct the discovery of the next-generation rare-earth substituted inorganic phosphors.
Results
Machine learning for predicting Debye temperature and screening inorganic phosphor hosts
The machine-learning model to predict Debye temperature first requires training using a large, diverse set of data. In this case, the 2610 DFT-based bulk (BDFT) and shear (GDFT) moduli extracted from the Materials Project database can be converted into an approximate Debye temperature (ΘD,DFT) based on the average sound velocity (νm) following Eq. 1, where h is Planck constant, kB is Boltzmann constant, n is the number of atoms per formula unit, NA is Avogadro constant, ρ is the crystal structure’s density, M is the molar mass, and νm is the average sound velocity33:
1 |
In a polycrystalline material, νm can be approximated following Eq. 2:
2 |
where νL and νT are the longitudinal and transverse sound velocity, respectively, which can be obtained from the DFT calculated BDFT and GDFT using Eq. 3:
3 |
Once ΘD,DFT was obtained for all 2610 compounds, a machine-learning algorithm was developed to predict the Debye temperature using support vector machine regression (SVR) (ΘD,SVR). The 10-fold cross-validation regression analysis for ΘD,SVR is plotted in Fig. 1a. The statistics of the cross-validated fit show excellent agreement between the ΘD,DFT and the ΘD,SVR with a root mean-squared error of cross-validation of 59.9 K and a mean absolute error of 37.9 K. The coefficient of determination (r2) is 0.89 indicating that the descriptor set does an excellent job expressing the materials Debye temperatures. Nearly all of the data (97%) falls between 50 and 750 K, as highlighted by the darker regions of the plot. The cross-validated ΘD,SVR tends to be slightly underestimated, particularly for materials with extremely high Debye temperatures (>1500 K), which is potentially due to the lack of data with extremely high Debye temperature. In fact, there are only four compounds, BN, Be2C, B6O, and LiB6C, that fall notably below the expected ΘD,SVR, suggesting that our machine-learning model does not capture the chemistry of these very light compounds. Although there are a few incorrect predictions, Fig. 1b shows that more than 75% of the compounds are predicted within ≈15% of the DFT calculated value.
Once the training set has been constructed, the machine-learning algorithm can be used to estimate ΘD,SVR for compounds compiled in crystallographic databases. The extraction of the crystal structures from PCD followed the same criteria as listed above, supplying 118,287 unique compounds for prediction. This list includes 15,770 binary compounds, 56,266 ternary compounds, and 46,251 quaternary compounds, of which 27,698 (23%) contain rare-earth elements that cannot be readily calculated using conventional DFT and 19,384 (16%) have either disordered positions or site mixing, which is also generally inaccessible with DFT. From this extended list, the search for potential phosphor hosts can be immediately reduced by adhering to a few simple phosphor design criteria. First, knowledge of the band gap is essential for screening phosphor hosts using the sorting diagram, and each compound was further cross-referenced against the Materials Project to ensure that the (Perdew, Burke, and Ernzerhof (PBE)-level) Eg,DFT is available. Additionally, a majority of rare-earth substituted phosphor hosts contain at least three elements, that is, are ternary phases or higher; therefore, in this study binary compounds are excluded. These two basic requirements reduced the number of possible compounds by 94% to 7504. The list of potential rare-earth substituted inorganic phosphor hosts could be further honed considering rare-earth substituted phosphor hosts are customarily composed of only the elements highlighted by the blue boxes shown in Fig. 2; any compound that does not follow this set of composition requirements was therefore also removed from the list of potential phosphors10. Finally, any compound following all of these criteria but still calculated to be a metal, that is, Eg = 0, was also removed from the list narrowing the final number of possible phosphor hosts to 2071. The ΘD,SVR of these 2071 compositions was subsequently predicted with the machine-learning model and associated with the DFT calculated band gap (Eg,DFT). This entire dataset was used to screen potential inorganic phosphor hosts and is provided as Supporting Information.
Plotting the 2071 compounds’ Eg,DFT as a function of their predicted ΘD,SVR, illustrated in Fig. 3a, creates an expanded sorting diagram that is convenient for balancing these two properties. The darker regions on this plot represent a higher density of potential phosphor hosts. Some (8%) of the compounds on the sorting diagram have very narrow (0 eV < Eg,DFT ≤ 0.4 eV) PBE-level band gaps, suggesting that these phases are not likely viable options as rare-earth substituted phosphor hosts. There are also a considerable number (22%) with a ΘD,SVR <250 K, indicating that these materials may not have the structural rigidity necessary for a high Φ.
Decomposing the sorting diagram into the compositional information indicates several trends related to the potential of different phosphor hosts. For example, Fig. 3b shows that borates tend to have wide band gaps and surprisingly high Debye temperatures owing to boron’s small size that allows dense polyhedral packing. Sulfides have a ΘD,SVR < 500 K and an Eg,DFT only in the range of 0–4 eV, which suggests that any emission will likely have a rather low Φ when substituted with a rare-earth ion. Conversely, nitrides (Fig. 3c) have moderate band gaps (<4.5 eV), but a generally high ΘD,SVR due to the covalently bonded, corner-sharing [SiN4] tetrahedra. This allows the predicted Debye temperature to surpass 600 K for many of the compounds and supports the numerous efficient nitride based rare-earth inorganic phosphors. Silicates (Fig. 3d) and aluminates (Fig. 3e), which are perhaps the most common classes of phosphor hosts, tend to have wide band gaps, but they also have a range of prospective ΘD,SVR values. Experimentally there are many silicates and aluminates with a high luminescence quantum efficiency, most notably Y3Al5O12:Ce3+ or (Ba/Sr)2SiO4:Eu2+, as well as numerous reports of materials that have low luminescence quantum efficiency reinforcing the range of Debye temperatures and band gaps14,17. In contrast, fluorides (Fig. 3d) all show very wide band gaps ranging between 4 and 8 eV but low Debye temperatures (<500 K) due to the ionic bonding in these phases. Finally, phosphates (Fig. 3e) tend to have wide bandgaps >4 eV) and moderate Debye temperatures (≈500 K) signifying there is potential for continued development in this space. In fact, a significant number of rare-earth substituted phosphates have been recently reported such as Na3Sc2(PO4)3:Eu2+ 15, BaRbPO4:Eu2+34, and LiSrPO4:Eu2+35, supporting the sorting diagram’s suggestion.
Analyzing metadata-like composition is clearly indispensable for directing the search for new materials, with the potential to shift the search toward remarkable composition space, such as focusing on borates. Indeed, a few high-efficiency borate phosphors have already been reported. For example, Ce3+-substituted Ba2Y5B5O17 has a blue emission with an Φ of 70% at room temperature that can be increased to nearly 90% by substituting the harder cation Lu3+ for the comparatively softer Y3+36,37. Similarly, NaSrBO3:Ce3+ and NaCaBO3:Ce3+ both have a reported Φ of ≈75%38,39. Many of the borate phosphors including K2Al2B2O7:Eu2+ are also thermally robust showing minimal loss of luminescence at high temperature40. Although the search for borate phosphors is directed based on the machine-learning algorithm, the discovery of these materials was still achieved through traditional means including isovalent substitution of known materials, rationally searching phase space, or through serendipitous discovery.
The development of an enhanced sorting diagram also makes it possible to target specific compounds as prospective high Φ phosphors. For example, examining the sorting diagram shows that CaAlB3O7 has a very high ΘD,SVR of 732 K and Eg,DFT of 5.3 eV due to the presence of alternating layers of [AlO6] octahedral and [BO4] tetrahedra connected through edge and corner sharing, with the Ca2+ decorated among the very dense anionic network41. Li5Rb2B7O14 is also a phase of interest given that ΘD,SVR is 703 K and Eg,DFT is 4.5 eV. This phase is a non-centrosymmetric crystal structure that contains a three-dimensional network of polyborate chains producing the expected rigid crystal structure42. Both of these phases are viable phosphor hosts and worth consideration. Additionally, perhaps the most unique crystal structure suggested by the sorting diagram is NaBaB9O15 (highlighted in Fig. 3b). This compound stands out among the 2071 potential phosphors due to its high ΘD,SVR of 729 K and Eg,DFT of 5.5 eV. NaBaB9O15 is a particularly remarkable compound because the composition suggests that the bonding should be primarily ionic and not a rigid crystal structure as implied by the ΘD,SVR. Therefore, experimentally investigating this unanticipated potential phosphor host will lend support to the sorting diagram as a tool for identifying new high Φ rare-earth substituted inorganic phosphors.
Phosphor synthesis and crystal structure refinement
The synthesis of NaBaB9O15 yielded a phase pure product according to laboratory (Cu Kα) powder X-ray diffraction. The structure of the unsubstituted, that is, x = 0, sample was analyzed using high-intensity, high-resolution synchrotron X-ray powder diffraction data, shown in Fig. 4. The crystal structure was obtained from the Rietveld refinement with details provided in Table 1 and the refined atomic coordinates and isotropic displacement parameters listed in Table 2.
Table 1.
Formula | NaBaB9O15 |
---|---|
Radiation type; λ (Å) | Synchrotron radiation; 0.457667 |
2θ range (deg.) | 0.5000–49.998 |
Temperature (K) | 295 |
Space group; Z | ; 6 |
Lattice parameters (Å) | a = 11.10166(6) |
c = 17.40089(4) | |
Unit cell volume (Å3) | 1857.28(5) |
Calculated mass density (g cm–3) | 2.669 |
Formula weight (g mol–1) | 497.595 |
Profile R-factor, Rp | 0.0739 |
Weighted profile R-factor, Rwp | 0.0907 |
χ 2 | 2.820 |
Table 2.
Atom | Wyckoff position | x | y | z | ueq (Å2) |
---|---|---|---|---|---|
Ba(1) | 6a | 0 | 0 | 0.00101(1) | 0.0119(1) |
Na(1) | 6a | 0 | 0 | 0.22197(9) | 0.0152(7) |
B(1) | 18b | 0.38819(4) | 0.26465(7) | 0.05556(1) | 0.008(9) |
B(2) | 18b | 0.45065(5) | 0.39436(4) | 0.17207(5) | 0.0082(4) |
B(3) | 18b | 0.22489(5) | 0.32886(5) | 0.11364(3) | 0.0072(8) |
O(1) | 18b | 0.48014(6) | 0.32856(7) | 0.11349(6) | 0.0111(7) |
O(2) | 18b | 0.25453(3) | 0.24296(1) | 0.06014(7) | 0.0063(3) |
O(3) | 18b | 0.20422(2) | 0.4309(3) | 0.0678(5) | 0.0070(4) |
O(4) | 18b | 0.34374(4) | 0.41612(6) | 0.16374(7) | 0.004(1) |
O(5) | 18b | 0.1069(8) | 0.23238(5) | 0.16009(1) | 0.0077(8) |
NaBaB9O15 adopts the non-centrosymmetric trigonal space group R3c (no. 161). As illustrated in Fig. 5, the crystal structure contains a three-dimensional framework of [B3O7]5– subunits in which two [BO3]3– trigonal planar units and one [BO4]5– tetrahedron are linked by the vertices. The refined B–O bond lengths within the trigonal planes range between 1.33 and 1.38 Å, while the bond lengths within the [BO4]5– tetrahedron are slightly longer (1.45–1.49 Å). The arrangement of the [B3O7]5– units generates large tunnels along the [001] direction that are occupied by Ba2+ and Na+. The Ba2+ ions are coordinated in a nine-vertex distorted tri-capped trigonal prism, whereas six oxygen atoms form a highly distorted trigonal antiprism surrounding the Na+ ions. This combination of corner sharing [B3O7]5– polyhedra is remarkable because it constructs a network that is not especially dense. In fact, the calculated density of NaBaB9O15 is only 2.669 g cm–3 which is half the density of the other reported Na-Ba-B-O phases43,44. Such a porous anionic network would not be predicted to form a rigid crystal structure. However, the high ΘD likely arises due to the presence of high-frequency vibrational modes from the unique [B3O7]5− structural unit, which forms an extended and intertwined polyanionic backbone. Moreover, the high concentration of very light boron atoms also gives rise to the presence of high-frequency phonon modes. This combination of composition and crystal structure both contribute to the anomalously high Debye temperature for NaBaB9O15. Because machine learning has minimal bias, the prediction is undiscriminating in which crystal structures are suggested, highlighting the importance of using this approach to identify phases that may otherwise be disregarded.
Once the crystal structure is refined from high-resolution scattering data, it is possible to experimentally estimate ΘD based on the Debye–Waller theory as a confirmation of the machine-learning prediction45,46. Although this is a considerable approximation that assumes a single acoustic branch and ignores the optical modes, it is still valuable for comparing the machine-learning predicted Debye temperature to an experimental value. Using the mean-square atomic displacement parameters, <>, the ΘD,i can be calculated for each crystallographically independent atom, i, following Eq. 4, where m is the atomic mass and ueq,i is the atomic displacement parameter. The overall Debye temperature (ΘD) can then be approximated by taking the stoichiometrically weighted average of ΘD,i according to the formula NaBaB9O15:
4 |
Evaluating for ΘD using the refined <> (Table 2) suggests that the Debye temperature should be ≈635 K, which is only 12% lower than the machine learning predicted ΘD,SVR. This is in an excellent agreement considering that the B and G values used in the training set are derived from DFT using the Voigt–Reuss–Hill approximation and neglects the temperature dependence of the elastic moduli. Moreover, the scattering refinement data are based on synchrotron X-ray diffraction, which is not particularly adept at evaluating atomic displacement parameters. Nevertheless, the small difference indicates that machine learning is indeed a viable technique for quickly estimating ΘD,SVR.
Photoluminescent properties of the identified phosphor
The high ΘD,SVR and wide PBE-level calculated band gap suggests that NaBaB9O15 has strong potential as an inorganic phosphor host. Considering that the PBE-level calculations significantly underestimate Eg, a HSE06 hybrid functional calculation was conducted using the Vienna ab initio Simulation Package47–49 to ensure that this compound has a sufficient band gap to tolerate the rare-earth’s electronic transitions. The result confirms NaBaB9O15 indeed has a very wide calculated Eg,HSE of 7.3 eV. The phosphor was then prepared by substituting Eu2+ as the luminescent center for Ba2+ following NaBa1–xEuxB9O15 (x = 0, 0.005, 0.01, 0.02, 0.03, 0.04, and 0.05). The compound maintains phase purity across the entire substitution range examined, as plotted in Supplementary Figure 1. Measuring the photoluminescence excitation spectrum indicates that Eu2+ has a broad ultra-violet excitation band ranging from 230 to 385 nm, as shown in Fig. 6a. The spectrum contains a main excitation peak centered at λex = 275 along with two shoulders at λex = 315 and λex = 365 nm. The emission spectra collected by exciting at these three wavelengths produces an identical emission peak with a maximum emission wavelength at 416 nm, indicating that the multiple excitation peaks arise from the electronic transitions between the Eu2+ 4f orbitals to multiple Eu2+ 5d orbital excited states. The emission spectra can be fit by a single Gaussian peak, depicted in Fig. 6a (and Supplementary Figure 2b), corresponding to the emission from a single crystallographically independent Eu2+. This is in agreement with the refined crystal structure that only contains one substitution site, Ba(1). The single Eu2+ site was further supported by measuring the photoluminescence lifetime (Supplementary Figure 3). The data could be fit with a single exponential function described in Eq. 5:
5 |
where I is the luminescent intensity, t is time, A is parameter, and τ is the decay time, to reveal that the luminescence decay occurs with a 0.842 μs decay time. The emission is a bright violet with Commission Internationale de l'Eclairage (CIE) 1931 coordinate of (0.1620, 0.01522) and has a very narrow full-width at half-maximum (FWHM) of only 1962 cm–1 (34.5 nm). These data show that this material eclipses the industry standard blue-emitting phosphor BaMgAl10O17:Eu2+, which has a FWHM of ≈2200 cm−1 (≈50 nm)50, but NaBaB9O15:Eu2+ is still broader than the recently reported blue-emitting AELi2[Be4N6]:Eu2+ (AE = Sr, Ba) phosphors that have a FWHM of only ≈1200 cm−1 (≈25 nm)51.
Given that the crystal structure of NaBaB9O15 host is likely a highly rigid phosphor host based on the predicted ΘD,SVR, the Φ of NaBaB9O15:Eu2+ system was extensively analyzed. First, the rare-earth concentration was optimized by varying the loading of Eu2+. As shown in Fig. 6b, the 3 mol% Eu2+ concentration in NaBaB9O15:Eu2+ has the highest Φ = 95(1)%, and increasing the Eu2+ concentration causes an abrupt drop in Φ. Exciting the phosphor at 340 nm shows the same optimized concentration of Eu2+ with a slight decrease in Φ to ≈75% with an increase in the rare-earth content beyond 3 mol% again causing a drop in Φ. The origin of the emission loss stems from an energy transfer process between adjacent luminescence centers. The critical distance between luminescent centers for this concentration quenching process (RC) can be calculated following Eq. 6, where V is the volume of the unit cell, xc is the optimized rare-earth concentration, and N is the number of crystallographically independent Eu2+ positions in a unit cell52. In NaBaB9O15:Eu2+, using a volume of 1857.28 Å, an optimized concentration of x = 0.03, and six Eu2+ crystallographic sites, the critical distance is approximately 27 Å. Such a large RC means that self-quenching is not a very prominent mechanism for non-radiative relaxation in this crystal structure, partly explaining the excellent Φ:
6 |
Beyond concentration quenching, inorganic phosphors can also undergo thermal quenching, where the luminescence intensity is lost due to an increase in non-radiative relaxation. Probing the temperature dependence of the emission spectrum from 80 to 500 K (Supplementary Figure 4) reveals that NaBa0.97Eu0.03EuB9O15 possesses an outstanding thermal response. As shown in Fig. 7a, the emission spectrum broadens slightly with increasing temperature going from FWHM = 32.5 nm (1849.5 cm–1) at 80 K to FWHM = 40.1 nm (2286.1 cm–1) at 500 K. This change can be attributed to increased electron–phonon line broadening at elevated temperatures associated with the excited state 5d orbitals of Eu2+5. More importantly, the emission spectrum at high temperature does not show any thermal quenching, which is the loss of luminescence with increasing temperature, even as the temperature approaches 500 K (Fig. 7b). There is a slight loss of emission intensity once the temperature is >360 K; however, this decrease is only by ≈15%. The integrated area of the emission peak shows no change across the entire temperature range examined because the loss of emission intensity is accompanied by a widening of the FWHM of the emission spectrum, countering the loss of intensity and leading to minimal thermal quenching up to 500 K.
Temperature-dependent powder X-ray diffraction data (Supplementary Figure 5a) indicate that there is no structural modification at elevated temperatures based on refining the crystal structure’s unit cell volume as a function of temperature (Supplementary Figure 5b). Thus, the origin of the outstanding thermal properties in this phosphor can be explained by evaluating the two classical non-radiative pathways that dominate thermal quenching53. One process is through thermally induced photoionization, where increasing the temperature can lead to the excited-state electrons occupying the Eu2+ 5d orbitals being thermally promoted into the phosphor host’s conduction band preventing re-emission. The best method to restrict photoionization is by ensuring that the phosphor host has strong crystal field splitting and a very wide Eg. Separating the rare-earth orbitals from the host conduction band mitigates the probability of thermal excitation at any reasonable temperature, and, therefore, prevents this quenching pathway. Although the crystal field splitting is not considerable, bearing in mind that the borate polyanion is a weak-field ligand, the Eg,HSE for NaBaB9O15:Eu2+ is still 7.3 eV. This sizeable band gap is likely sufficient to separate rare-earth orbitals from the host conduction band, thereby minimizing this quenching pathway.
The second non-radiative relaxation process occurs via electron–phonon coupling of the ground state and excited state potential energy surfaces53. In rare-earth substituted phosphors, the excitation of an electron from the ground state to the excited state causes a simultaneous relative displacement (Δr) of the excited state nuclear coordinates with respect to the ground state nuclear coordinates. If the Δr separating the potential energy surfaces is large, then the two potential energy surfaces can cross (interact), which supplies a mechanism for non-radiative relaxation via electron–phonon coupling13. Conversely, in systems where Δr is small, the potential energy surfaces do not interact and the relaxation process can proceed uninhibited, ideally by luminescence. Empirically the best approach for preventing a large Δr, as it relates to changes in bond lengths, might be to target rigid crystal structures13,54. However, recent research has showed that ΘD, as a proxy for rigidity, is not always predictive of thermal quenching55,56.
Alternatively, a method to probe Δr in a solid state material is to estimate the electron–phonon coupling by ascertaining a material’s Huang–Rhys factor S57,58. Experimentally, S can be extracted by measuring the FWHM of the rare-earth substituted phosphor’s emission peak as a function of temperature and fitting these data with Eq. 7:
7 |
where ℏω is the mean phonon energy and kB is the Boltzmann constant59,60. A system that has strong electron–phonon coupling (large Δr) tends to have S > 5, whereas weak electron–phonon coupling (small Δr) occurs when S < 1. Fitting the temperature-dependent luminescence data for NaBaB9O15:Eu2+ (Supplementary Figure 6) reveals the Huang–Rhys factor is only 2.098, indicating that this material is approaching the weak electron–phonon coupling regime, and, therefore, should have a relatively small Δr. The consequence is that the two potential energy surfaces in this phosphor are not expected to intersect and the electron–phonon coupling is predicted to be minimal. Thus, this mechanism is also not anticipated to be a primary contributor to non-radiative relaxation in this phosphor. The combination of limited concentration quenching, the absence of photoionization as a quenching mechanism, and the lack of overlap between the ground and excited state potential energy surfaces leads to the robust thermal behavior for NaBaB9O15:Eu2+.
Conclusions
In conclusion, the Debye temperature of 2071 potential phosphor hosts was predicted with the assistance of machine learning and correlated with their (PBE-level) DFT calculated band gaps. The construction of a sorting diagram based on these two intrinsic material properties is suitable to navigate vast phase space to identify classes of the next generation of inorganic phosphors. For example, borates are worth significant investigation due to their outstanding Debye temperatures and wide (PBE-level) band gaps. One specific borate highlighted by the sorting diagram is NaBaB9O15:Eu2+, which has a ΘD,SVR of 729 K and a Eg,DFT of 5.5 eV. The subsequent synthesis of this phosphor via solid-state reaction showed that the material could be readily prepared as a phase pure product with multiple heating steps. The crystal structure was analyzed using high-resolution synchrotron X-ray powder diffraction and showed a unique polyanionic [B3O7]5– network, which generates a three-dimensional backbone necessary for a structural rigidity. Substituting the compound with Eu2+ yields a violet emission at λmax = 416 nm when excited with near-ultraviolet (UV) light (315 nm) light, while the optimal Eu2+ concentration produces a maximum Φ of 95%. Moreover, the FWHM of the emission is only 34.5 nm, making NaBaB9O15:Eu2+ a narrow violet-emitting phosphor. Temperature-dependent luminescent measurements indicate that this compound is also extremely thermally robust with minimal thermal quenching of up to 500 K due to the lack of non-radiative relaxation pathways. These experimental results support that machine learning is an indispensable tool necessary to direct the search for next generation of rare-earth substituted inorganic phosphors. Although the phosphor discovered in this work is not immediately applicable in current LED-based white lighting devices, it has great potential for use in other applications such as UV-excited laser lighting. Furthermore, the excellent thermal properties of this crystal structure suggest that it is an excellent platform to modify the excitation/emission peaks through chemical substitution. Shifting the optical properties to longer wavelength will make this material viable as a next-generation rare-earth substituted inorganic phosphor.
Methods
Data extraction and machine-learning model
To develop the supervised machine-learning model for predicting ΘD, the bulk modulus B and shear modulus G of 3248 compounds were obtained from the Material Project database as well as from our own calculations61. These values were then cross-referenced with PCD30 to ensure that all the compositions used for machine learning are experimentally reported, that is, not a predicted crystal structure. Additionally, only binary, ternary, and quaternary compositions were considered, and any compound containing group 18 elements, hydrogen, Tc, or Z > 83 (except for U and Th), were omitted. Finally, thin films, foils, or suspensions were excluded. These criteria reduced the number of elastic moduli in our final training dataset to 2610 compounds, including 1343 binary phases, 1229 ternary phases, and 38 quaternary phases. To distinguish between the polymorphs, the materials were labeled as “composition, space group number.”
The machine-learning model was then constructed based on an SVR analysis using PLS_Toolbox (version 8.2.1) within the MATLAB® (R2017a) environment62. The training set employed DFT calculated Debye temperatures obtained as described below. Our SVR applied a radial basis function as the kernel function and was optimized using venetian blinds cross-validation (CV) with 10-fold data splits. The compounds considered by the machine-learning algorithm were evaluated using a descriptor set of 34 distinct compositional variables along with four math expressions including the difference, average, and the largest and smallest values, as well as 14 crystal structure variables such as space group number, crystal system, and electron density, among others. The full descriptor set is provided in Supplementary Table 1. These 150 descriptors (as x-vector data) were used to build the machine-learning training model, which was represented in a 2610 × 150 matrix that was normalized, mean-centered, and rescaled to the unit variance. Calculated Debye temperature, ΘD, was used as y-vector data (or dependent variable). This model used an optimized cost parameter (C) and gamma (γ) functions of 32 and 0.0032, respectively, where C regulates the tradeoff between minimization of error and maximization of the margins and γ is the kernel parameter controlling the influence of each support vector. This SVR model was then used to predict the Debye temperature of compounds contained within PCD.
Phosphor synthesis
One phosphor host of particular interest identified in PCD by machine learning is NaBaB9O1563,64. Therefore, NaBa1–xEuxB9O15 (x = 0, 0.005, 0.01, 0.02, 0.03, 0.04, 0.05) was prepared via solid-state reactions starting from NaHCO3 (EM science, 99.7%), BaCO3 (Johnson Matthey, 98%), H3BO3 (Sigma-Aldrich, 99.999%), and Eu2O3 (Materion Advanced Chemicals, 99.9%). The starting materials were loaded in the requisite stoichiometric ratios, thoroughly ground using an agate mortar and pestle, and subsequently sintered at 600 °C for 2 h in air to decompose the reagents and initiate the reaction. The samples were then ground and heated at 700 °C for 15 h, followed by a second grinding and heating at 750 °C for 5 h to obtain a phase pure product. These two heating steps were performed in alumina crucibles using a fused silica tube furnace under a reducing atmosphere (5% H2/95% N2) with heating and cooling ramps of 3 °C min–1. The products were finally ground in an agate mortar and pestle then sieved (<325 mesh) prior to characterization.
Crystal structure determination and optical characterization
The samples were all checked for phase purity using powder X-ray diffraction on a PanAnalytical X’Pert powder diffractometer equipped with Cu Kα radiation (λ = 1.54183 Å). Additionally, powder synchrotron X-ray diffraction data was collected on NaBaB9O15 at 295 K with a calibrated wavelength of 0.457667 Å (beamline 11-BM, Advanced Photon Source, Argonne National Laboratory)65. The crystal structure was refined based on the Rietveld method using the GSAS package with a shifted Chebyshev function employed to describe the background and a pseudo-Voigt function for determining peak shape66,67. The final crystal structure was visualized using VESTA68.
Steady-state photoluminescent spectra were collected at room temperature on a Photon Technology International fluorescence spectrophotometer with a 75 W xenon arc lamp for excitation. The samples were mixed into an optically transparent silicone resin (GE Silicones, RTV615) and deposited on a quartz substrate (Chemglass) for the room temperature measurements. Temperature-dependent measurements required the sample to be mixed with KBr in a 10:1 molar ratio of KBr:NaBa0.97Eu0.03B9O15 and then pressed into a 13 mm pellet. The temperature was controlled using a Janis liquid nitrogen cryostat (VPF-100) and the emission spectra were collected from 80 to 500 K in 20 K increments using a λex = 340 nm. The absolute (internal) photoluminescent quantum yield was determined by placing the samples encapsulated in the silicone resin inside a Spectralon-coated integrating sphere (150 mm diameter, Labsphere) and exciting at 315 nm69. The luminescence lifetime decay measurements were collected using a Horiba DeltaFlex Lifetime System equipped with a NanoLED N-330 nm LED (λex = 336 nm) and a 400 nm longpass filter. A total measurement length of 3.2 μs was employed using a repetition rate of 250 kHz and a delay of 10 ns.
Electronic supplementary material
Acknowledgements
We thank the Department of Chemistry and the Division of Research at the University of Houston for providing generous start-up funds as well as the National Science Foundation through No. NSF-CMMI 15-62142 for supporting this research. A.O.O. acknowledges generous funding support through the Elby Nell McElrath Postdoctoral Fellowship. Use of the Advanced Photon Source at Argonne National Laboratory was supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract No. DE-AC02-06CH11357.
Author contributions
Y.Z. conducted the machine learning modelling, inorganic synthesis, and characterization. Y.Z., A.M.T., and A.O.O. prepared the data for the training set of the machine learning model. A.M.T. performed the DFT calculations and assisted with machine learning. A.C.D. fit the temperature-dependent luminescence data to obtain the Huang–Rhys factor. Y.Z. and J.B. wrote the paper. J.B. designed and supervised the research. All authors discussed the results and commented on the manuscript.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Competing interests
The authors declare no competing interests.
Footnotes
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Supplementary Information accompanies this paper at 10.1038/s41467-018-06625-z.
References
- 1.Pimputkar S, Speck JS, DenBaars SP, Nakamura S. Prospects for LED lighting. Nat. Photonics. 2009;3:180–182. doi: 10.1038/nphoton.2009.32. [DOI] [Google Scholar]
- 2.Pust P, Schmidt PJ, Schnick W. A revolution in lighting. Nat. Mater. 2015;14:454–458. doi: 10.1038/nmat4270. [DOI] [PubMed] [Google Scholar]
- 3.Schubert EF, Kim JK. Solid-state light sources getting smart. Science. 2005;308:1274–1278. doi: 10.1126/science.1108712. [DOI] [PubMed] [Google Scholar]
- 4.Höppe HA. Recent developments in the field of inorganic phosphors. Angew. Chem. Int. Ed. 2009;48:3572–3582. doi: 10.1002/anie.200804005. [DOI] [PubMed] [Google Scholar]
- 5.Qin X, Liu X, Huang W, Bettinelli M, Liu X. Lanthanide-activated phosphors based on 4f–5d optical transitions: theoretical and experimental aspects. Chem. Rev. 2017;117:4488–4527. doi: 10.1021/acs.chemrev.6b00691. [DOI] [PubMed] [Google Scholar]
- 6.Lin CC, Liu RS. Advances in phosphors for light-emitting diodes. J. Phys. Chem. Lett. 2011;2:1268–1277. doi: 10.1021/jz2002452. [DOI] [PubMed] [Google Scholar]
- 7.Smet PF, Parmentier AB, Poelman D. Selecting conversion phosphors for white light-emitting diodes. J. Electrochem. Soc. 2011;158:R37–R54. doi: 10.1149/1.3568524. [DOI] [Google Scholar]
- 8.George NC, Denault KA, Seshadri R. Phosphors for solid-state white lighting. Annu. Rev. Mater. Res. 2013;43:481–501. doi: 10.1146/annurev-matsci-073012-125702. [DOI] [Google Scholar]
- 9.Rong-Jun X, Naoto H, Takashi T. Wide color gamut backlight for liquid crystal displays using three-band phosphor-converted white light-emitting diodes. Appl. Phys. Express. 2009;2:022401. doi: 10.1143/APEX.2.022401. [DOI] [Google Scholar]
- 10.Shionoya, S., Yen, W. M. & Yamamoto, H. Phosphor Handbook (CRC Press, Boca Raton, 2006).
- 11.Blasse G. Thermal quenching of characteristic fluorescence. J. Chem. Phys. 1969;51:3529–3530. doi: 10.1063/1.1672543. [DOI] [Google Scholar]
- 12.Dorenbos P. Thermal quenching of Eu2+ 5d–4f luminescence in inorganic compounds. J. Phys. Condens. Matter. 2005;17:8103. doi: 10.1088/0953-8984/17/50/027. [DOI] [Google Scholar]
- 13.Tian Y. Development of phosphors with high thermal stability and efficiency for phosphor-converted LEDs. J. Solid State Light. 2014;1:11. doi: 10.1186/s40539-014-0011-8. [DOI] [Google Scholar]
- 14.Bachmann V, Ronda C, Meijerink A. Temperature quenching of yellow Ce3+ luminescence in YAG:Ce. Chem. Mater. 2009;21:2077–2084. doi: 10.1021/cm8030768. [DOI] [Google Scholar]
- 15.Kim YH, et al. A zero-thermal-quenching phosphor. Nat. Mater. 2017;16:543–550. doi: 10.1038/nmat4843. [DOI] [PubMed] [Google Scholar]
- 16.Hermus M, Brgoch J. Phosphors by design: approaches toward the development of advanced luminescent materials. Electrochem. Soc. Interface. 2015;24:55–59. doi: 10.1149/2.F06154if. [DOI] [Google Scholar]
- 17.Denault KA, et al. Consequences of optimal bond valence on structural rigidity and improved luminescence properties in SrxBa2–xSiO4:Eu2+ orthosilicate phosphors. Chem. Mater. 2014;26:2275–2282. doi: 10.1021/cm500116u. [DOI] [Google Scholar]
- 18.Denault KA, et al. Average and local structure, Debye temperature, and structural rigidity in some oxide compounds related to phosphor hosts. ACS Appl. Mater. Inter. 2015;7:7264–7272. doi: 10.1021/acsami.5b00445. [DOI] [PubMed] [Google Scholar]
- 19.Furman JD, Melot BC, Teat SJ, Mikhailovsky AA, Cheetham AK. Towards enhanced ligand-centred photoluminescence in inorganic–organic frameworks for solid state lighting. Phys. Chem. Chem. Phys. 2011;13:7622–7629. doi: 10.1039/C0CP01717E. [DOI] [PubMed] [Google Scholar]
- 20.Brgoch J, DenBaars SP, Seshadri R. Proxies from ab initio calculations for screening efficient Ce3+ phosphor hosts. J. Phys. Chem. C. 2013;117:17955–17959. doi: 10.1021/jp405858e. [DOI] [Google Scholar]
- 21.Agrawal A, Choudhary A. Perspective: materials informatics and big data: realization of the “fourth paradigm” of science in materials science. APL Mater. 2016;4:053208. doi: 10.1063/1.4946894. [DOI] [Google Scholar]
- 22.Rajan K. Materials informatics: the materials “gene” and big data. Annu. Rev. Mater. Res. 2015;45:153–169. doi: 10.1146/annurev-matsci-070214-021132. [DOI] [Google Scholar]
- 23.Pilania G, et al. Machine learning bandgaps of double perovskites. Sci. Rep. 2016;6:19375. doi: 10.1038/srep19375. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 24.Pilania G, Wang C, Jiang X, Rajasekaran S, Ramprasad R. Accelerating materials property predictions using machine learning. Sci. Rep. 2013;3:2810. doi: 10.1038/srep02810. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 25.Isayev O, et al. Universal fragment descriptors for predicting properties of inorganic crystals. Nat. Commun. 2017;8:15679. doi: 10.1038/ncomms15679. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 26.Ward L, Agrawal A, Choudhary A, Wolverton C. A general-purpose machine learning framework for predicting properties of inorganic materials. NPJ Comput. Mater. 2016;2:16028. doi: 10.1038/npjcompumats.2016.28. [DOI] [Google Scholar]
- 27.Hu JM, Duan CG, Nan CW, Chen LQ. Understanding and designing magnetoelectric heterostructures guided by computation: progresses, remaining questions, and perspectives. NPJ Comput. Mater. 2017;3:18. doi: 10.1038/s41524-017-0020-4. [DOI] [Google Scholar]
- 28.Liu R, et al. A predictive machine learning approach for microstructure optimization and materials design. Sci. Rep. 2015;5:11551. doi: 10.1038/srep11551. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 29.Sundararaghavan V, Zabaras N. Classification and reconstruction of three-dimensional microstructures using support vector machines. Comput. Mater. Sci. 2005;32:223–239. doi: 10.1016/j.commatsci.2004.07.004. [DOI] [Google Scholar]
- 30.Villars, P. & Cenzual, K. Pearson’s Crystal Data—Crystal Structure Database for Inorganic Compounds (ASM International, Materials Park, 2014).
- 31.Setlur, A. A. et al. Ce3+-based phosphors for blue LED excitation. Proc. of SPIE 5187, 142–149 (2004).
- 32.Dorenbos P. Energy of the Eu2+ 5d state relative to the conduction band in compounds. J. Lumin. 2008;128:578–582. doi: 10.1016/j.jlumin.2007.09.005. [DOI] [Google Scholar]
- 33.Anderson OL. A simplified method for calculating the Debye temperature from elastic constants. J. Phys. Chem. Solids. 1963;24:909–917. doi: 10.1016/0022-3697(63)90067-2. [DOI] [Google Scholar]
- 34.Song HJ, et al. RbBaPO4:Eu2+: a new alternative blue-emitting phosphor for UV-based white light-emitting diodes. J. Mater. Chem. C. 2013;1:500–505. doi: 10.1039/C2TC00162D. [DOI] [Google Scholar]
- 35.Liu J, Wu Z, Gong M. Thermally stable luminescence of blue LiSrPO4:Eu2+ phosphor for near-UV light-emitting diodes. Appl. Phys. B. 2008;93:583–587. doi: 10.1007/s00340-008-3169-1. [DOI] [Google Scholar]
- 36.Hermus M, Phan PC, Brgoch J. Ab initio structure determination and photoluminescent properties of an efficient, thermally stable blue phosphor, Ba2Y5B5O17:Ce3+ Chem. Mater. 2016;28:1121–1127. doi: 10.1021/acs.chemmater.5b04542. [DOI] [Google Scholar]
- 37.Hermus M, Phan PC, Duke AC, Brgoch J. Tunable optical properties and increased thermal quenching in the blue-emitting phosphor series: Ba2(Y1–xLux)5B5O17:Ce3+ (x=0–1) Chem. Mater. 2017;29:5267–5275. doi: 10.1021/acs.chemmater.7b01416. [DOI] [Google Scholar]
- 38.Zhang X, Song J, Zhou C, Zhou L, Gong M. High efficiency and broadband blue-emitting NaCaBO3: Ce3+ phosphor for NUV light-emitting diodes. J. Lumin. 2014;149:69–74. doi: 10.1016/j.jlumin.2014.01.012. [DOI] [Google Scholar]
- 39.Liu WR, et al. High efficiency and high color purity blue-emitting NaSrBO3:Ce3+ phosphor for near-UV light-emitting diodes. J. Mater. Chem. 2011;21:6869–6874. doi: 10.1039/c1jm10765h. [DOI] [Google Scholar]
- 40.Xiao W, et al. Blue-emitting K2Al2B2O7:Eu2+ phosphor with high thermal stability and high color purity for near-UV-pumped white light-emitting diodes. Inorg. Chem. 2015;54:3189–3195. doi: 10.1021/ic502773t. [DOI] [PubMed] [Google Scholar]
- 41.Villars, P. & Cenzual, K. CaAl[B3O7] Crystal Structure: Datasheet from “PAULING FILE Multinaries Edition—2012”. in SpringerMaterials (https://materials.springer.com/isp/crystallographic/docs/sd_1221608) (Springer, Berlin Heidelberg and Material Phase Data System (MPDS), Switzerland and National Institute for Materials Science (NIMS), Japan).
- 42.Yang Y, et al. Li5Rb2B7O14: a new congruently melting compound with two kinds of B-O one-dimensional chains and short UV absorption edge. CrystEngComm. 2012;14:6720–6725. doi: 10.1039/c2ce06742k. [DOI] [Google Scholar]
- 43.Tu JM, Keszler DA. BaNaBO3. Acta Crystallogr. Sect. C. 1995;51:1962–1964. doi: 10.1107/S010827019400750X. [DOI] [Google Scholar]
- 44.Wu L, et al. Structure determination and relative properties of novel cubic borates MM'4 (BO3)3 (M = Li, M’ = Sr; M = Na, M’ = Sr, Ba) Inorg. Chem. 2005;44:6409–6414. doi: 10.1021/ic050299s. [DOI] [PubMed] [Google Scholar]
- 45.Willis, B. T. M. & Pryor, A. W. Thermal Vibrations in Crystallography (Cambridge University Press, Cambridge, 1975).
- 46.George NC, et al. Average and local structural origins of the optical properties of the nitride phosphor La(3-x)Ce(x)Si6N11 (0 < x ≤ 3) Inorg. Chem. 2013;52:13730–13741. doi: 10.1021/ic402318k. [DOI] [PubMed] [Google Scholar]
- 47.Kresse G, Joubert D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B. 1999;59:1758–1774. doi: 10.1103/PhysRevB.59.1758. [DOI] [Google Scholar]
- 48.Kresse G, Furthmüller J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B. 1996;54:11169–11186. doi: 10.1103/PhysRevB.54.11169. [DOI] [PubMed] [Google Scholar]
- 49.Heyd J, Scuseria GE, Ernzerhof M. Hybrid functionals based on a screened Coulomb potential. J. Chem. Phys. 2003;118:8207–8215. doi: 10.1063/1.1564060. [DOI] [Google Scholar]
- 50.Wang Y, Xu X, Yin L, Hao L. High thermal stability and photoluminescence of Si–N-codoped BaMgAl10O17:Eu2+ phosphors. J. Am. Ceram. Soc. 2010;93:1534–1536. [Google Scholar]
- 51.Philipp S, Christian M, Volker W, J. SP, Wolfgang S. Ultra‐narrow band blue emitting oxoberyllates AELi2[Be4O6]:Eu2+ (AE=Sr,Ba) paving the way to efficient RGB pc‐LEDs. Angew. Chem. 2018;130:8875–8879. doi: 10.1002/ange.201804721. [DOI] [PubMed] [Google Scholar]
- 52.Blasse G. Energy transfer in oxidic phosphors. Philips Res. Rep. 1969;24:131. [Google Scholar]
- 53.Struck, C. W. & Fonger, W. H. Understanding Luminescence Spectra and Efficiency using Wp and Related Functions (Springer, Berlin, 1991).
- 54.Setlur AA, Shiang JJ, Hannah ME, Happek U. Phosphor quenching in LED packages: measurements, mechanisms, and paths forward. SPIE Opt. Eng.+Appl. 2009;7422:8. [Google Scholar]
- 55.Duke AC, Finley E, Hermus M, Brgoch J. Yellow-green luminescence and extreme thermal quenching in the Sr6M2Al4O15:Eu2+ (M = Y, Lu, Sc) phosphor series. Solid State Sci. 2016;60:108–113. doi: 10.1016/j.solidstatesciences.2016.08.013. [DOI] [Google Scholar]
- 56.Ha J, et al. An integrated first principles and experimental investigation of the relationship between structural rigidity and quantum efficiency in phosphors for solid state lighting. J. Lumin. 2016;179:297–305. doi: 10.1016/j.jlumin.2016.07.006. [DOI] [Google Scholar]
- 57.de Jong M, Seijo L, Meijerink A, Rabouw FT. Resolving the ambiguity in the relation between Stokes shift and Huang–Rhys parameter. Phys. Chem. Chem. Phys. 2015;17:16959–16969. doi: 10.1039/C5CP02093J. [DOI] [PubMed] [Google Scholar]
- 58.Huang K, Rhys A. Theory of light absorption and non-radiative transitions in F-centres. Proc. R. Soc. Lond. Ser. A. 1950;204:406–423. doi: 10.1098/rspa.1950.0184. [DOI] [Google Scholar]
- 59.Blasse G., Grabmaier B. C. Luminescent Materials. Berlin, Heidelberg: Springer Berlin Heidelberg; 1994. A General Introduction to Luminescent Materials; pp. 1–9. [Google Scholar]
- 60.Cooke DW, Bennett BL, McClellan KJ, Roper JM, Whittaker MT. Oscillator strengths, Huang–Rhys parameters, and vibrational quantum energies of cerium-doped gadolinium oxyorthosilicate. J. Appl. Phys. 2000;87:7793–7797. doi: 10.1063/1.373456. [DOI] [Google Scholar]
- 61.Jain A, et al. Commentary: The Materials Project: a materials genome approach to accelerating materials innovation. APL Mater. 2013;1:011002. doi: 10.1063/1.4812323. [DOI] [Google Scholar]
- 62.Drucker, H., Burges, C. J. C., Kaufman, L., Smola, A. & Vapnik, V. in Advances in Neural Information Processing Systems (eds Mozer, M.C., Jordan, J. I., Petscbe, T.) 155–161 (MIT Press, Cambridge, 1997).
- 63.Penin N, Seguin L, Touboul M, Nowogrocki G. Synthesis and crystal structure of three MM’B9O15 borates (M = Ba, Sr and M’ = Li; M = Ba and M’ = Na) Int. J. Inorg. Mater. 2001;3:1015–1023. doi: 10.1016/S1466-6049(01)00078-2. [DOI] [Google Scholar]
- 64.Ingle JT, Sonekar RP, Omanwar SK, Moharil SV. Synthesis and photoluminescence of blue phosphors NaBaB9O15:Eu2+ Int. J. Chem. Anal. Sci. 2011;2:23–24. [Google Scholar]
- 65.Lee PL, et al. A twelve-analyzer detector system for high-resolution powder diffraction. J. Synchrotron Radiat. 2008;15:427–432. doi: 10.1107/S0909049508018438. [DOI] [PubMed] [Google Scholar]
- 66.. Larson, A. C. & Von Dreele, R. B. General Structure Analysis System (GSAS) 86–748 (Los Alamos National Laboratory Report LAUR, Santa Fe, 2004).
- 67.Toby BH. EXPGUI, a graphical user interface for GSAS. J. Appl. Crystallogr. 2001;34:210–213. doi: 10.1107/S0021889801002242. [DOI] [Google Scholar]
- 68.Momma K, Izumi F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 2011;44:1272–1276. doi: 10.1107/S0021889811038970. [DOI] [Google Scholar]
- 69.Leyre S, et al. Absolute determination of photoluminescence quantum efficiency using an integrating sphere setup. Rev. Sci. Instrum. 2014;85:123115. doi: 10.1063/1.4903852. [DOI] [PubMed] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.
Supplementary Materials
Data Availability Statement
The data that support the findings of this study are available from the corresponding author upon reasonable request.