| Hoffmann's Harmonic Shades (ZPC) |
Hoffmann Dental Manufaktur GmbH, Berlin, Germany |
Zinc-phosphate cement |
5826 |
O-phosphoric acid, zinc oxide, magnesium oxide |
| Ketac Cem Radiopaque (GIC) |
3M ESPE, St. Paul, MN, USA |
Glass-ionomer cement |
526731 |
Copolymer acrylic acid-maleic acid (< 20 wt%), glass powder (80 – 90 wt%) |
| Durelon (PCC) |
3M ESPE, St. Paul, MN, USA |
Polycarboxylate cement |
538749 |
Polyacrylic acid (40 – 50 wt%), water (50 – 65 wt%), zinc oxide (85 – 95 wt%), stannous fluoride (1 – 10 wt%), tin dioxide (1 – 5 wt%) |
| Rely X U200 (RXU) |
3M ESPE, St. Paul, MN, USA |
Resin-based, self-adhesive, dual cure |
586 495 |
GPDM, self-etching/adhering acidic monomer, 7 wt% (46 vol%) barium glass, FAS glass, fumed silica |
| C&B (C&B) |
BISCO, Inc., Schaumburg, IL, USA |
Self-cured composite cement |
1400003636 |
Fused silica, bisphenol A glycidylmethacrylate, triethylene glycol dimethacrylate, sodium fluoride |
| RelyX Temp NE (RXT) |
3M ESPE, St. Paul, MN, USA |
Resin based temporary luting cement |
5547792 |
Resin, reaction products with acrylic acid (60 – 70 wt%), nonanoic acid (30 – 40 wt%), silane treated silica (1 – 5 wt%), Zinc oxide (80 – 90 wt%), white mineral oil (5 – 15 wt%), petrolatum (1 – 5 wt%) |
| Telio CS Cem Implant (TCS) |
Ivoclar Vivadent AG, Schaan, Liechtenstein |
Resin based temporary luting cement |
T22772 |
Bismethacrylates (approx. 52 wt%), Ytterbium trifluoride (10 – < 25 wt%) |