Table 7.
Physical properties of the macroporous resins employed.
| Macroporous resin | Polarity | Particle size (mm) | Surface area (m2/g) | Average pore diameter (nm) | Moisture content (%) |
|---|---|---|---|---|---|
| X-5 | Non-polar | 0.30–1.25 | 500–600 | 29–30 | 50.13 ± 0.17 |
| D-101 | Non-polar | 0.30–1.25 | 480–530 | 9–11 | 67.89 ± 0.27 |
| HPD-100 | Non-polar | 0.30–1.25 | ≥650 | 8–9 | 68.39 ± 0.48 |
| D1300 | Non-polar | 0.30–1.25 | ≥600 | 9–10 | 68.27 ± 0.57 |
| D3520 | Non-polar | 0.30–1.25 | 480–520 | 8–9 | 71.56 ± 0.18 |
| AB-8 | Weak-polar | 0.30–1.25 | 480–520 | 13–14 | 68.33 ± 0.61 |
| DM130 | Weak-polar | 0.30–1.25 | 500–550 | 9–10 | 66.00 ± 0.32 |
| DS-8 | Weak-polar | 0.30–1.25 | 500–550 | 12–14 | 63.55 ± 0.10 |
| DM-301 | Middle-polar | 0.30–1.25 | ≥330 | 14–17 | 65.48 ± 1.32 |
| ADS-17 | Middle-polar | 0.30–1.25 | 90–150 | 25–30 | 55.16 ± 1.09 |
| S-8 | Polar | 0.30–1.25 | 100–200 | 28–30 | 67.12 ± 0.35 |
| NKA-9 | Polar | 0.30–1.25 | 250–290 | 15–16 | 70.22 ± 0.23 |
| DA-201 | Polar | 0.30–1.25 | ≥200 | 10–13 | 70.64 ± 0.52 |
| HP-20 | Non-polar | ≥ 0.25 | 590 | 38 | 60.25 ± 0.53 |
| SP825L | Non-polar | ≥ 0.25 | 930 | 14 | 57.63 ± 0.03 |
| SP850 | Non-polar | ≥ 0.25 | 930 | 9 | 48.34 ± 0.05 |
| SP700 | Non-polar | ≥ 0.25 | 1200 | 18 | 67.47 ± 0.05 |
| SP70 | Non-polar | ≥ 0.25 | 870 | 14 | 61.24 ± 0.15 |
| SP207 | Non-polar | ≥ 0.25 | 600 | 22 | 50.27 ± 0.49 |
| HP2MGL | Middle-polar | ≥ 0.30 | 570 | 48 | 64.87± 0.94 |
Note: Informations were provided by the manufactures except moisture content.