Table 1. Parameters for the polymeric scaffold, found from experiments or the literature^5,26,32, which are used as inputs to the computational G&R model.

Parameter	Description	Value	Units
$r_{PGA}^p$	PGA felt pore size	39.3	μm
${\omega }_{PGA}^p$	PGA felt fiber diameter	15.9	μm
$E_{PGA}^p$	PGA Young’s-type modulus23	7	GPa
$k_{PGA}^p$	PGA degradation rate	0.128	1/days
${\zeta }_{PGA}^p$	PGA degradation shape parameter	28.5	days
rp	PGA-P(CL/LA) scaffold pore size	11.2	μm
ω p	PGA-P(CL/LA) scaffold fiber diameter	4.01	μm
$E_{P(CL∕LA)}^p$	P(CL/LA) Young’s-type modulus5	0.1	GPa
$k_{P(CL∕LA)}^p$	P(CL/LA) degradation rate	0.138	1/days
${\zeta }_{P(CL∕LA)}^p$	P(CL/LA) shape parameter	130.25	days