Table 4.

Mechanical properties of FMC00, FMC10, and FMC20 both for type ‘A’ and type ‘B’ samples. Values are given for n = 4 samples showing the full range as error.

Sample	Young's Modulus	0.2% Proof	UTS	Hardness	Strain at Break
	(GPa)	(MPa)	(MPa)	(GPa)	%
FMC00 type ‘A’	${163}_{-8}^{+14}$	${382}_{-55}^{+87}$	${978}_{-111}^{+115}$	$4.4\pm 0.3$	${58}_{-11}^{+9}$
FMC00 type ‘B’	${159}_{-9}^{+9}$	${291}_{-23}^{+23}$	${902}_{-38}^{+38}$		${57}_{-5}^{+5}$
FMC10 type ‘A’	${157}_{-8}^{+10}$	${405}_{-70}^{+82}$	${859}_{-340}^{+230}$	$5.7\pm 0.4$	${43}_{-0}^{+0}$
FMC10 type ‘B’	${167}_{-15}^{+19}$	${462}_{-64}^{+49}$	${1063}_{-191}^{+170}$		${43}_{-13}^{+8}$
FMC20 type ‘A’	${178}_{-10}^{+24}$	${464}_{-148}^{+134}$	${1301}_{-86}^{+135}$	$8.5\pm 0.5$	${27}_{-3}^{+6}$
FMC20 type ‘B’	${171}_{-26}^{+15}$	${590}_{-22}^{+15}$	${1232}_{-120}^{+41}$		${31}_{-4}^{+3}$