Table 9.
Batch compositions of the glasses within the fluorapatite (FA)–diopside (Di) joint (mol %).
| Glass | CaO | MgO | SiO2 | P2O5 | CaF2 |
|---|---|---|---|---|---|
| FA-100 | 69.23 | 0.00 | 0.00 | 23.08 | 7.69 |
| FA-90 | 63.15 | 3.43 | 6.87 | 19.91 | 6.64 |
| FA-80 | 57.57 | 6.59 | 13.19 | 16.99 | 5.66 |
| FA-70 | 52.40 | 9.51 | 19.03 | 14.30 | 4.77 |
| FA-60 | 47.62 | 12.21 | 24.44 | 11.80 | 3.93 |
| FA-50 | 43.18 | 14.73 | 29.45 | 9.48 | 3.16 |
| FA-40 | 39.04 | 17.07 | 34.12 | 7.33 | 2.45 |
| FA-35 | 37.07 | 18.18 | 36.34 | 6.30 | 2.10 |
| FA-30 | 35.18 | 19.25 | 38.49 | 5.31 | 1.77 |
| FA-25 | 33.34 | 20.28 | 40.57 | 4.36 | 1.45 |
| FA-20 | 31.57 | 21.29 | 42.57 | 3.43 | 1.14 |
| FA-10 | 28.18 | 23.20 | 46.41 | 1.66 | 0.55 |
| FA-0 | 25.00 | 25.00 | 50.00 | 0.00 | 0.00 |