Table 2.

Mechanical properties of neat polymers and glass-filled composites.

	TPU composites						PDMS composites
	P	P5	P15	P25	P35	P50	S	S5	S15	S25	S35	S50
Young’s Modulus [MPa]	14.59 ± 2.97	35.97 ± 6.14	24.13 ± 0.40	32.24 ± 2.19	65.56 ± 1.05	73.85 ± 4.12	1.94 ± 0.48	4.16 ± 0.98	3.79 ± 0.49	6.19 ± 1.12	7.88 ± 1.94	16.16 ± 5.06
Tensile strength [MPa]	13.50 ± 3.68	11.13 ± 6.87	18.98 ± 2.76	14.54 ± 2.74	11.89 ± 3.25	10.42 ± 0.40	1.54 ± 0.55	1.81 ± 0.64	1.24 ± 0.44	2.57 ± 0.14	2.95 ± 0.67	4.33 ± 1.74
Elongation at break [%]	342 ± 0.40	442 ± 0.73	581 ± 0.44	456 ± 0.10	360 ± 0.40	332 ± 0.19	112 ± 0.34	64 ± 0.05	46 ± 0.19	62 ± 0.02	47 ± 0.06	39 ± 0.10