Table 6.

Results of cone calorimetry (neat resin: sample thickness 4 mm, composites: sample thickness 2 mm) and UL94 (sample thickness 4 mm) for depicted samples.

Sample	tti/s	pHRR/kW·m−2	THR·X−1/MJ·m−2	MARHE/kW·m−2	TSR·X−1/m2·m−2	THR·ML−11/kW·m−2·g−1	Residue/%	X	UL94-V *
RTM6	94 ± 1	1715 ± 58	104 ± 1	550 ± 6	5601 ± 31	2.25	4 ± 2	1	NR
+ 10% BA-DOPO	-	-	-	-	-	-	-	1	V1
+ 10% TAHHT-DOPO	98 ± 12	1092 ± 54	89 ± 2	401 ± 22	6458 ± 51	1.85	2 ± 0	1	V0
+ 10% TAHHT-DDPO	81 ± 2	1419 ±8	85 ± 2	421 ± 3	3853 ± 17	2.19	3 ± 0	1	V0
+ 10% TAHHT-DOPO-DDPO	85 ± 1	1278 ± 30	85 ± 3	416 ± 8	5160 ± 123	1.97	2 ± 0	1	V0
RTM6 + CF	31 ± 2	492 ± 19	72 ± 1	242 ± 5	3763 ± 165	2.51	59 ± 1	0.43	V1
+ 10% BA-DOPO	32 ± 5	384 ± 53	63 ± 3	203 ±16	5815 ± 600	2.05	56 ± 1	0.49	V0
+ 10% TAHHT-DOPO	34 ± 1	476 ± 75	70 ± 3	234 ± 115	5070 ± 283	2.17	54 ± 1	0.52	V0
+ 10% TAHHT-DDPO	29 ± 4	388 ± 52	67 ± 4	218 ± 22	4277 ± 369	2.37	59 ± 1	0.50	V0
+ 10% TAHHT-DOPO-DDPO	37 ± 3	456 ± 58	69 ± 2	228 ± 13	5269 ± 136	2.21	55 ± 1	0.52	V0

X: ratio of the combustible material mass to the whole sample mass. * NR: not rated.